EFFECT OF CATHODIC PROTECTION CONDITIONS ON THE STRESS CORROSION CRACKING OF LINE PIPE STEELS.

被引：0
|
作者：
Kasahara, Komei
Adachi, Haruhiko
机构：
来源：
Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan | 1983年 / 69卷 / 14期
关键词：
STEEL CORROSION - Stress Corrosion Cracking;
D O I：
10.2355/tetsutohagane1955.69.14_1630
中图分类号：
学科分类号：
摘要：
A cathodic protection current of not less than 1 mA/cm**2 could cause cathodic disbonding of the protective coating and could form a sufficient concentration of alkali to produce carbonate-bicarbonate SCC. Pipelines cathodically protected at a polarization potential between minus 1000 and minus 1350 mv vs. Cu-CuSO//4 and cathodic current density of less than 1 mA/cm**2 were free from SCC.
引用
收藏
页码：1630 / 1637
相关论文
共 50 条
  • [41] Influence of the applied stress rate on the stress corrosion cracking of 4340 and 3.5NiCrMoV steels under conditions of cathodic hydrogen charging
    Ramamurthy, S.
    Lau, W. M. L.
    Atrens, A.
    CORROSION SCIENCE, 2011, 53 (07) : 2419 - 2429
  • [42] Hydrogen-related stress corrosion cracking in line pipe steel
    Nielsen, LV
    ADVANCES IN CORROSION CONTROL AND MATERIALS IN OIL AND GAS PRODUCTION, 1999, (26): : 120 - 126
  • [43] PREVENTION OF SULPHIDE STRESS CORROSION CRACKING IN THE WELDS OF LINE PIPE.
    Tanaka, Takahide
    Ito, Yoshinori
    Nakanishi, Mutsuo
    Kaneko, Teruo
    Komizo, Yuichi
    Sumitomo Search, 1980, (23): : 27 - 34
  • [44] EFFECT OF BORIDING ON CORROSION RESISTANCE OF STEELS.
    Loskutov, V.F.
    Permyakov, V.G.
    Pisarenko, V.N.
    Trush, I.Kh.
    Protection of Metals, 1975, 11 (01): : 40 - 41
  • [45] Influence of Metallurgical Parameters on Hydrogen Induced Cracking of Pipe Sheet Steels.
    Margot-Marette, H.
    Charbonnier, J.C.
    Bridoux, D.
    Perdrix, C.
    Cahiers d'Informations Techniques - Revue de Metallurgie, 1986, 83 (12): : 891 - 899
  • [46] Criteria for Accelerated Estimation of Susceptibility of Pipe Steels to Corrosion Cracking Under Oilfield Conditions
    Kondrat'ev, S. Yu
    Al'khimenko, A. A.
    Khar'kov, A. A.
    Shvetsov, O., V
    Davydov, A. D.
    METAL SCIENCE AND HEAT TREATMENT, 2022, 63 (9-10) : 533 - 539
  • [47] Criteria for Accelerated Estimation of Susceptibility of Pipe Steels to Corrosion Cracking Under Oilfield Conditions
    S. Yu. Kondrat’ev
    A. A. Al’khimenko
    A. A. Khar’kov
    O. V. Shvetsov
    A. D. Davydov
    Metal Science and Heat Treatment, 2022, 63 : 533 - 539
  • [48] Stress corrosion cracking of prestressing steels
    Mietz, J
    Fischer, J
    Isecke, B
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 1999, 50 (09): : 535 - 540
  • [49] Stress corrosion cracking of stainless steels
    Steel Products Lab., Nippon Steel Corp., Japan
    Yosetsu Gakkai Shi, 2006, 3 (27-30):
  • [50] Stress corrosion cracking of pipeline steels
    Fang, BY
    Han, EH
    Zhu, ZY
    Wang, JQ
    Ke, W
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2002, 18 (01) : 3 - 6
12345