EFFECT OF CATHODIC PROTECTION CONDITIONS ON THE STRESS CORROSION CRACKING OF LINE PIPE STEELS.

被引：0
|
作者：
Kasahara, Komei
Adachi, Haruhiko
机构：
来源：
Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan | 1983年 / 69卷 / 14期
关键词：
STEEL CORROSION - Stress Corrosion Cracking;
D O I：
10.2355/tetsutohagane1955.69.14_1630
中图分类号：
学科分类号：
摘要：
A cathodic protection current of not less than 1 mA/cm**2 could cause cathodic disbonding of the protective coating and could form a sufficient concentration of alkali to produce carbonate-bicarbonate SCC. Pipelines cathodically protected at a polarization potential between minus 1000 and minus 1350 mv vs. Cu-CuSO//4 and cathodic current density of less than 1 mA/cm**2 were free from SCC.
引用
收藏
页码：1630 / 1637
相关论文
共 50 条
  • [31] Cathodic Corrosion Protection of Pipeline Steels
    Schoeneich, Hanns-Georg
    37. VDI-JAHRESTAGUNG SCHADENSANALYSE: PRODUKTVERBESSERUNG DURCH SCHADENSANALYSE, 2011, 2150 : 175 - 188
  • [32] WELDABILITY OF HIGH STRENGTH LINE PIPE STEELS.
    North, T.H.
    Rothwell, A.B.
    Glover, A.G.
    Pick, R.J.
    Welding Journal (Miami, Fla), 1982, 61 (08):
  • [33] STRESS CORROSION CRACKING OF WELDED LINE PIPE STEEL.
    Ackland, B.G.
    Australian Welding Research, 1980, 9 : 31 - 37
  • [34] Study, by the Methods of Fracture Mechanics, of Fatigue Cracking and Stress Corrosion Cracking of Very High Strength Steels.
    Baus, A.
    Charbonnier, J.C.
    Lieurade, H.P.
    Marandet, B.
    Roesch, L.
    Sanz, G.
    1600, (72):
  • [35] EFFECT OF GRIT BLASTING ON THE STRESS-CORROSION CRACKING BEHAVIOR OF LINE PIPE STEEL
    KOCH, GH
    BARLO, TJ
    BERRY, WE
    MATERIALS PERFORMANCE, 1984, 23 (10) : 20 - 23
  • [36] Corrosion cracking of low alloy steels. Testing methods
    Alhimenko, A. A.
    Breki, A. D.
    Shaposhnikov, N. O.
    Kharkov, A. A.
    Alekseeva, E. L.
    Lapechenkov, A. A.
    MATERIALS PHYSICS AND MECHANICS, 2022, 50 (03): : 459 - 474
  • [37] Application of Fracture Mechanics to Sulfide Corrosion Cracking of Steels.
    Lang, Cestmir
    1600, (11):
  • [38] The role of residual stress in neutral pH stress corrosion cracking of pipeline steels. Part 1: Pitting and cracking occurrence
    Van Boven, G.
    Chen, W.
    Rogge, R.
    ACTA MATERIALIA, 2007, 55 (01) : 29 - 42
  • [39] A method for testing pipe steels under the conditions of sulfide stress cracking
    Astaf'ev V.I.
    Narushev V.M.
    Tetyueva T.V.
    Materials Science, 1999, 35 (4) : 587 - 591
  • [40] A method for testing pipe steels under the conditions of sulfide stress cracking
    Astaf'ev, VI
    Narushev, VM
    Tetyueva, TV
    MATERIALS SCIENCE, 1999, 35 (04) : 587 - 591
12345