DECLINE OF CORROSION RESISTANCE BY Cr-DEPLETION LAYER IN SUS 304 STAINLESS STEEL.

被引：0
|
作者：
Ogushi, Tetsutaro [1 ]
机构：
[1] Nippon Kinzoku Co, Technical, Research & Development Lab,, Tokyo, Jpn, Nippon Kinzoku Co, Technical Research & Development Lab, Tokyo, Jpn
来源：
| 1600年 / 34期
关键词：
PICKLING;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
When stainless steels are annealed in a gas burning furnace to form a surface oxide scale enriched in Cr, a Cr depletion zone is generated due to the delay of Cr diffusion from the matrix to the surface. Therefore, insufficient pickling causes lower corrosion resistance. After pickling, a depth-profile of Cr and corrosion resistance against Cl** minus ion were measured. Surface Cr concentration and corrosion resistance increased with increasing pickling time. It is concluded that a pickling time of 35-45 sec is suitable.
引用
收藏
相关论文
共 50 条
  • [21] DEFORMATION IN TYPE 304 AUSTENITIC STAINLESS STEEL.
    Anon
    1600,
  • [22] Corrosion resistance of friction stir welded 304 stainless steel
    Park, SHC
    Sato, YS
    Kokawa, H
    Okamoto, K
    Hirano, S
    Inagaki, M
    SCRIPTA MATERIALIA, 2004, 51 (02) : 101 - 105
  • [23] Effect of ultrasonic wave on the growth of corrosion pits on SUS304 stainless steel
    Wang, Rongguang
    Nakasa, Keijiro
    MATERIALS TRANSACTIONS, 2007, 48 (05) : 1017 - 1022
  • [24] Effect of Different Lap Angles on Corrosion Resistance of SUS304 Stainless Steel Joints Welded by TIG Welding
    Wang, Jing
    Huo, Yushuang
    INTERNATIONAL JOURNAL OF PRECISION ENGINEERING AND MANUFACTURING, 2024, 25 (12) : 2563 - 2571
  • [25] Influence of pipe diameter on galvanic corrosion between sus304 stainless steel and galvanized steel
    Yamate, Toshihiro
    Zairyo to Kankyo/ Corrosion Engineering, 2013, 62 (11): : 434 - 438
  • [26] Effect of Cr-C Coatings on the Corrosion Resistance of 304 Stainless Steel in the Molten Sodium Polysulfide
    Ren, Yanjie
    Du, Chenyang
    Du, Huayue
    Chen, Jian
    Zhao, Yuhang
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2021, 16 (02): : 1 - 9
  • [27] Corrosion resistance improvement of SUS430 stainless steel by plating
    Ogushi, Tetsutaro
    Yamazaki, Osamu
    Osada, Eiichi
    Yashiro, Toshiyuki
    Boshoku gijutsu, 1987, 36 (11): : 645 - 649
  • [28] EVALUATION OF INTERGRANULAR CORROSION IN STAINLESS STEEL.
    Loginow, A.W.
    1600, (04):
  • [29] INTERGRANULAR CORROSION OF LOW CARBON LOW NITROGEN 17% Cr STAINLESS STEEL.
    Okazaki, Takashi
    Miyoshi, Masanori
    Abo, Hideo
    Hirai, Taku
    Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, 1977, 63 (05): : 631 - 640
  • [30] CORROSION BEHAVIOR OF 19Cr-2Mo FERRITIC STAINLESS STEEL.
    Onoyama, Masao
    Tsuji, Masanobu
    Takemura, Susumu
    Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, 1977, 63 (05): : 641 - 658
12345