CRACK GROWTH IN THE VICINITY OF WELDS.

被引：0

作者：

Adams, N.J.I.

机构：

来源：

Welding Journal (Miami, Fla) | 1973年 / 52卷 / 11期

关键词：

WELDING; ELECTRIC - Electron Beam;

D O I：

暂无

中图分类号：

TG4 [焊接、金属切割及金属粘接];

学科分类号：

080201 ; 080503 ;

摘要：

Fatigue crack growth in the vicinity of welded joints in wide plates has been examined. In one series of tests the applied load was normal to the crack plane and growth was initiated in the center of the weld bead. Crack growth in gas tungsten-arc and electron beam welds was studied. The second series of tests involved crack growth normal to the weld line to examine the effect of residual stress on crack growth. An analytical procedure was developed to predict crack growth when compressive residual stresses are present.

引用

共 50 条

[21] Solidification, Segregation and Defects in Welds.
Savage, W.F.
Rivista Italiana della Saldatura, 1981, 33 (06): : 339 - 351
[22] GUIDE FOR THE NONDESTRUCTIVE INSPECTION OF WELDS.
Anon
American National Standards Institute, Standards, 1980,
[23] FRACTURE TOUGHNESS TESTING OF WELDS.
Soete, W.
Denys, R.
Revue de la Soudure/Lastijdschrift, 1977, 33 (01): : 7 - 14
[24] Possibilities of Testing of Spot Welds.
Langrock, Stefan
ZIS-Mitteilungen, 1980, 22 (08): : 900 - 907
[25] STRAIT - INNOVATIVE STRAIGHTENING OF RAIL WELDS.
Esveld, Coenraad
Rail International, 1983, 14 (07): : 11 - 19
[26] Effects of Structural Design on Cracking in Welds.
Thiessen, Walter
Poweleit, Berend
Schweissen und Schneiden/Welding and Cutting, 1979, 31 (04): : 148 - 152
[27] UNDERWATER MAGNETIC PARTICLE INSPECTION OF WELDS.
Chedister, W.C.
Welding Journal (Miami, Fla), 1984, 63 (05): : 24 - 26
[28] Toughness Characteristics of Electric Arc Welds.
Eichhorn, F.
Ruegenberg, H.A.
Industrie-Anzeiger, 1977, 99 (74): : 1456 - 1458
[29] Hydrogen-Induced Crack Formation Problem in High-Pressure Vessels with Surfacing Welds.
Libra, Otakar
Soukup, Karel
Zvaranie Bratislava, 1985, 34 (10): : 297 - 303
[30] SOURCES OF POROSITY IN ALUMINIUM MIG WELDS.
Andrew, R.C.
1976, A Sess 5

← 1 2 3 4 5 →