Damage and deuterium retention of beryllium due to low energy deuterium ion irradiation

被引：0
|
作者：
Yoshida, Naoaki [1 ]
Mizusawa, Shuji [1 ]
Sakamoto, Ryuichi [1 ]
Muroga, Takeo [1 ]
机构：
[1] Kyushu Univ, Fukuoka, Japan
来源：
| 1996年 / ANS, La Grange Park卷 / 30期
关键词：
Annealing - Beryllium powder metallurgy - Desorption - Deuterium - Experimental reactors - Irradiation - Microstructure - Radiation damage - Thermal effects - Transmission electron microscopy;
D O I：
10.13182/fst96-a11963034
中图分类号：
学科分类号：
摘要：
Thermal desorption of deuterium(D) from 8-keV D-ion irradiated beryllium(Be) above room temperature was correlated with microstructural changes during irradiation and annealing to understand the underlying mechanism of retention and trapping of D. D bubbles are formed at all examined temperatures between 300K and 873K. Large roundish bubbles above 200nm are especially formed above 573K. They remain even after annealing up to 973K. Strong retention of D by the bubbles occurs for the irradiation up to 673K.
引用
收藏
相关论文
共 50 条
  • [41] In situ observation of damage evolution in TiC during hydrogen and deuterium ion irradiation at low temperatures
    Hojou, K
    Otsu, H
    Furuno, S
    Sasajima, N
    Izui, K
    JOURNAL OF NUCLEAR MATERIALS, 1996, 239 (1-3) : 279 - 283
  • [42] Insight into the co-deposition of deuterium with beryllium: Influence of the deposition conditions on the deuterium retention and release
    De Temmerman, G.
    Baldwin, M. J.
    Doerner, R. P.
    Nishijima, D.
    Seraydarian, R.
    Schmid, K.
    JOURNAL OF NUCLEAR MATERIALS, 2009, 390-91 : 564 - 567
  • [43] Simulation of Experimental Deuterium Retention in Tungsten under Periodic Deuterium Plasma Irradiation
    Oya, Makoto
    Hara, Yuki
    Katayama, Kazunari
    Ohya, Kaoru
    PLASMA AND FUSION RESEARCH, 2021, 16
  • [44] Simulation of Experimental Deuterium Retention in Tungsten under Periodic Deuterium Plasma Irradiation*)
    Oya M.
    Hara Y.
    Katayama K.
    Ohya K.
    Plasma and Fusion Research, 2021, 16 : 2405057 - 1
  • [45] Decreased surface blistering and deuterium retention in potassium-doped tungsten exposed to deuterium plasma following ion irradiation
    Ma, Xiaolei
    Zhang, Xiaoxin
    Wang, Ting
    Gao, Yuan
    Yuan, Yue
    Cheng, Long
    Zhu, Jipeng
    Lv, Wei
    Lang, Shaoting
    Ge, Changchun
    Yan, Qingzhi
    NUCLEAR FUSION, 2023, 63 (02)
  • [46] Deuterium retention in tungsten exposed to low-energy pure and helium-seeded deuterium plasmas
    Ogorodnikova, O. V.
    Schwarz-Selinger, T.
    Sugiyama, K.
    Alimov, V. Kh.
    JOURNAL OF APPLIED PHYSICS, 2011, 109 (01)
  • [47] EFFECT OF IRRADIATION ON DEUTERIUM REEMISSION AND RETENTION IN METALS
    TANABE, T
    TAKEO, M
    IMOTO, S
    JOURNAL OF NUCLEAR MATERIALS, 1989, 162 : 1077 - 1081
  • [48] Blistering and deuterium retention in Nb-doped W exposed to low-energy deuterium plasma
    Han, Wenjia
    Zhu, Kaigui
    Yan, Jing
    Xia, Tongjun
    Wang, Zhanlei
    Ye, Xiaoqiu
    Chen, Chang An
    Wu, Jiliang
    Ma, Yutian
    NUCLEAR MATERIALS AND ENERGY, 2020, 23 (23)
  • [49] Surface blistering and deuterium retention in tungsten exposed to low-energy deuterium plasma at different temperatures
    Qin, Shaoyang
    Wang, Jinliang
    Gao, Liang
    Cheng, Long
    Yuan, Yue
    Jacob, Wolfgang
    Lu, Guang-Hong
    NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 2019, 450 (210-214): : 210 - 214
  • [50] Effect of noble gas ion pre-irradiation on deuterium retention in tungsten
    Cheng, L.
    Zhao, Z. H.
    De Temmerman, G.
    Yuan, Y.
    Morgan, T. W.
    Guo, L. P.
    Wang, B.
    Zhang, Y.
    Wang, B. Y.
    Zhang, P.
    Cao, X. Z.
    Lu, G. H.
    PHYSICA SCRIPTA, 2016, T167
12345