Damage and deuterium retention of beryllium due to low energy deuterium ion irradiation

被引：0
|
作者：
Yoshida, Naoaki [1 ]
Mizusawa, Shuji [1 ]
Sakamoto, Ryuichi [1 ]
Muroga, Takeo [1 ]
机构：
[1] Kyushu Univ, Fukuoka, Japan
来源：
| 1996年 / ANS, La Grange Park卷 / 30期
关键词：
Annealing - Beryllium powder metallurgy - Desorption - Deuterium - Experimental reactors - Irradiation - Microstructure - Radiation damage - Thermal effects - Transmission electron microscopy;
D O I：
10.13182/fst96-a11963034
中图分类号：
学科分类号：
摘要：
Thermal desorption of deuterium(D) from 8-keV D-ion irradiated beryllium(Be) above room temperature was correlated with microstructural changes during irradiation and annealing to understand the underlying mechanism of retention and trapping of D. D bubbles are formed at all examined temperatures between 300K and 873K. Large roundish bubbles above 200nm are especially formed above 573K. They remain even after annealing up to 973K. Strong retention of D by the bubbles occurs for the irradiation up to 673K.
引用
收藏
相关论文
共 50 条
  • [31] Retention mechanisms and binding states of deuterium implanted into beryllium
    Reinelt, M.
    Allouche, A.
    Oberkofler, M.
    Linsmeier, Ch
    NEW JOURNAL OF PHYSICS, 2009, 11
  • [32] Deuterium retention in beryllium, molybdenum and tungsten at high fluences
    Haasz, AA
    Davis, JW
    JOURNAL OF NUCLEAR MATERIALS, 1997, 241 : 1076 - 1081
  • [33] Deuterium retention in re-solidified tungsten and beryllium
    Yu, J. H.
    Simmonds, M. J.
    Baldwin, M. J.
    Doerner, R. P.
    NUCLEAR MATERIALS AND ENERGY, 2019, 18 : 297 - 306
  • [34] Blister formation and deuterium retention on tungsten irradiated by low energy and high flux deuterium plasma
    Tokunaga, K
    Baldwin, MJ
    Doerner, RP
    Noda, N
    Kubota, Y
    Yoshida, N
    Sogabe, T
    Kato, T
    Schedler, B
    20TH IEEE/NPSS SYMPOSIUM ON FUSION ENGINEERING, PROCEEDINGS, 2003, : 242 - 245
  • [35] Surface modification and deuterium retention in rhenium doped tungsten exposed to low energy deuterium plasma
    Xia, Tongjun
    Yan, Jing
    Han, Wenjia
    Wang, Zizhao
    Jiang, Zhenyu
    Wu, Jianwei
    Shi, Yongzhi
    Wang, Zhanlei
    Ye, Xiaoqiu
    Wu, Jiliang
    Zhu, Kaigui
    FUSION ENGINEERING AND DESIGN, 2021, 173
  • [36] RETENTION OF DEUTERIUM IMPLANTED IN HOT-PRESSED BERYLLIUM
    KAWAMURA, H
    ISHITUKA, E
    SAGARA, A
    KAMADA, K
    NAKATA, H
    SAITO, M
    HUTAMURA, Y
    JOURNAL OF NUCLEAR MATERIALS, 1990, 176 : 661 - 665
  • [37] Blister formation and deuterium retention on tungsten exposed to low energy and high flux deuterium plasma
    Tokunaga, K
    Baldwin, MJ
    Doerner, RP
    Noda, N
    Kubota, Y
    Yoshida, N
    Sogabe, T
    Kato, T
    Schedler, B
    JOURNAL OF NUCLEAR MATERIALS, 2005, 337 (1-3) : 887 - 891
  • [38] Influence of beryllium carbide formation on deuterium retention and release
    Porosnicu, C.
    Anghel, A.
    Sugiyama, K.
    Krieger, K.
    Roth, J.
    Lungu, C. P.
    JOURNAL OF NUCLEAR MATERIALS, 2011, 415 (01) : S713 - S716
  • [39] DEUTERIUM TRAPPING IN ION-BOMBARDED BERYLLIUM
    LIU, MB
    SHEFT, I
    GRUEN, DM
    JOURNAL OF NUCLEAR MATERIALS, 1979, 79 (01) : 267 - 269
  • [40] A parametric study of helium retention in beryllium and its effect on deuterium retention
    Alegre, D.
    Baldwin, M. J.
    Simmonds, M.
    Nishijima, D.
    Hollmann, E. M.
    Brezinsek, S.
    Doerner, R. P.
    PHYSICA SCRIPTA, 2017, T170
12345