Study on influence of strain ratio on low cycle fatigue behavior of directionally solidified superalloy DZ125

被引：0
|
作者：
Liu, Jin-Long [1 ]
Shi, Duo-Qi [1 ]
Yang, Xiao-Guang [1 ]
Bao, Yu [1 ]
Wang, Jing-Ke [1 ]
机构：
[1] School of Jet Propulsion, Beihang University, Beijing 100191, China
来源：
Cailiao Gongcheng/Journal of Materials Engineering | 2010年 / 12期
关键词：
Low-cycle fatigue - Nickel alloys;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The low cycle fatigue (LCF) behaviors of a directionally solidified nickel-based superalloy DZ125 at 850°C and 980°C were investigated. The effect of strain ratio (R=-1, 0) on the stress-strain hysteresis loop, cyclic mean stress evolution and fatigue lives was analyzed. The results indicated that the scatter of fatigue life for R=-1 and R=0 was small enough to be neglected at 850°C and 980°C. The fracture cross section was observed using scan electronic microscopic (SEM) to analyze the crack initiation mechanism.
引用
收藏
页码：47 / 50
相关论文
共 50 条
  • [41] Effect of microstructures restoration on high temperature fatigue behavior of DZ125 superalloy
    Shifu Wang
    Allah Ditta
    Yi Xu
    Zheng Zhang
    ProgressinNaturalScience:MaterialsInternational, 2021, 31 (04) : 633 - 640
  • [42] Very High Cycle Fatigue Behavior of a Directionally Solidified Ni-Base Superalloy DZ4
    Nie, Baohua
    Zhao, Zihua
    Liu, Shu
    Chen, Dongchu
    Ouyang, Yongzhong
    Hu, Zhudong
    Fan, Touwen
    Sun, Haibo
    MATERIALS, 2018, 11 (01):
  • [43] The analysis on the low cycle fatigue behavior of a directionally solidified superalloy with recrystallized surface layers
    Shi, H. J.
    Ma, X. F.
    Jia, D. W.
    Zhang, H. F.
    Niu, L. S.
    MATERIALS AND PRODUCT TECHNOLOGIES, 2008, 44-46 : 43 - 50
  • [44] Influence of orientation and temperature on the fatigue crack growth of directionally solidification superalloys DZ125
    Shi, Yi
    Yang, Xiaoguang
    Yang, Didi
    Miao, Guolei
    Shi, Duoqi
    12TH INTERNATIONAL FATIGUE CONGRESS (FATIGUE 2018), 2018, 165
  • [45] Effect of Recrystallization Thickness on Creep Properties of Directionally Solidified DZ125 Alloy
    Qu Yanping
    Zhou Jinhua
    Yu Xingfu
    Wu Yuchao
    Peng Zhijian
    Zhang Mingju
    Huang Aihu
    RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (01) : 235 - 241
  • [46] Effect of surface recrystallization on the low cycle fatigue behavior of directionally solidified superalloy DZ4 by in-situ SEM studies
    Ma, Xianfeng
    Shi, Hui-ji
    THERMEC 2011, PTS 1-4, 2012, 706-709 : 2456 - 2461
  • [47] Recrystallizaiton behavior of directionally solidified DZ4 superalloy
    Li, YJ
    Zhang, WF
    Tao, CH
    14TH CONGRESS OF INTERNATIONAL FEDERATION FOR HEAT TREATMENT AND SURFACE ENGINEERING, VOLS 1 and 2, PROCEEDINGS, 2004, : 284 - 287
  • [48] Recrystallizaiton Behavior of Directionally Solidified DZ4 Superalloy
    Li Yun-ju
    材料热处理学报, 2004, (05) : 284 - 287
  • [49] EFFECTS OF STRAIN RATIO ON THERMAL-MECHANICAL CYCLIC STRESS-STRAIN RESPONSE AND FATIGUE LIFE IN DS SUPERALLOY DZ125
    G.D.Zhang
    S.L.Liu
    Y.H.He
    R.Z.Chen
    Acta Metallurgica Sinica(English Letters), 2004, (04) : 528 - 533
  • [50] Effect of process parameters on microstructures and properties of DZ125 superalloy solidified by LMC
    Zhang, H.
    Pei, Y.
    Li, S.
    Gong, S.
    MATERIALS RESEARCH INNOVATIONS, 2014, 18 : 385 - 389
12345