Study on influence of strain ratio on low cycle fatigue behavior of directionally solidified superalloy DZ125

被引：0
|
作者：
Liu, Jin-Long [1 ]
Shi, Duo-Qi [1 ]
Yang, Xiao-Guang [1 ]
Bao, Yu [1 ]
Wang, Jing-Ke [1 ]
机构：
[1] School of Jet Propulsion, Beihang University, Beijing 100191, China
来源：
Cailiao Gongcheng/Journal of Materials Engineering | 2010年 / 12期
关键词：
Low-cycle fatigue - Nickel alloys;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The low cycle fatigue (LCF) behaviors of a directionally solidified nickel-based superalloy DZ125 at 850°C and 980°C were investigated. The effect of strain ratio (R=-1, 0) on the stress-strain hysteresis loop, cyclic mean stress evolution and fatigue lives was analyzed. The results indicated that the scatter of fatigue life for R=-1 and R=0 was small enough to be neglected at 850°C and 980°C. The fracture cross section was observed using scan electronic microscopic (SEM) to analyze the crack initiation mechanism.
引用
收藏
页码：47 / 50
相关论文
共 50 条
  • [21] Microstructural evolution of directionally solidified DZ125 superalloy castings with different solidification methods
    Ge Bingming
    Liu Lin
    Zhang Jun
    Li Yafeng
    Fu Hengzhi
    Liu Xiaofu
    China Foundry, 2013, (01) : 24 - 28
  • [22] Effect of recrystallization on low-cycle fatigue behavior of DZ4 directionally-solidified superalloy
    Shi, HJ
    Zhang, HF
    Wu, YQ
    FRACTURE AND STRENGTH OF SOLIDS VI, PTS 1 AND 2, 2006, 306-308 : 175 - 180
  • [23] Effect of recrystallization on low-cycle fatigue behavior of DZ4 directionally-solidified superalloy
    Tsinghua University, Beijing 100084, China
    Hangkong Cailiao Xuebao, 2006, 1 (71-75):
  • [24] Microstructural evolution of directionally solidified DZ125 superalloy castings under different solidification methods
    Ge Bingming
    Liu Lin
    Zhang Jun
    Li Yafeng
    Fu Hengzhi
    Liu Xiaofu
    CHINA FOUNDRY, 2013, 10 (01) : 24 - 28
  • [25] Low cycle fatigue behavior of a directionally solidified cobalt base superalloy
    Lu, Z
    Xu, YB
    Hu, ZQ
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 270 (02): : 162 - 169
  • [26] Investigation on low cycle fatigue and fracture behaviors of directionally solidified DZ4 superalloy
    Zhang, WF
    Li, YJ
    Gao, W
    Fan, JJ
    Tao, CH
    RARE METAL MATERIALS AND ENGINEERING, 2005, 34 (02) : 217 - 220
  • [27] Constitutive modeling of a directionally solidified nickel-based superalloy DZ125 subjected to thermal mechanical creep fatigue loadings
    Xiao-An Hu
    Xiao-Guang Yang
    Duo-Qi Shi
    Hui-Chen Yu
    Ting-Ting Ren
    RareMetals, 2019, 38 (10) : 922 - 936
  • [28] Constitutive modeling of a directionally solidified nickel-based superalloy DZ125 subjected to thermal mechanical creep fatigue loadings
    Xiao-An Hu
    Xiao-Guang Yang
    Duo-Qi Shi
    Hui-Chen Yu
    Ting-Ting Ren
    Rare Metals, 2019, 38 : 922 - 936
  • [29] Constitutive modeling of a directionally solidified nickel-based superalloy DZ125 subjected to thermal mechanical creep fatigue loadings
    Hu, Xiao-An
    Yang, Xiao-Guang
    Shi, Duo-Qi
    Yu, Hui-Chen
    Ren, Ting-Ting
    RARE METALS, 2019, 38 (10) : 922 - 936
  • [30] Influence of Torsional Pre-deformation on the Low Cycle Fatigue Life of Directionally Solidified Superalloy DZ4
    Zhang Weifang
    Liu Xiao
    Liu Shengwang
    Wang Zongren
    Li Yunju
    RARE METAL MATERIALS AND ENGINEERING, 2012, 41 (09) : 1602 - 1606
12345