Synthesis of Ti-Fe alloys by mechanical alloying

被引：0

作者：

Hotta, Hideki ^{[1
]}

Abe, Masatake ^{[2
]}

Kuji, Toshiro ^{[2
]}

Uchida, Hirohisa ^{[1
]}

机构：

[1] Graduate School of Engineering, Tokai University, 1117 Kitakaname, Hiratsuka City, Kanagawa, 259-1292, Japan

[2] Course of Science and Technology, Graduate School of Science and Technology, Unified Graduate School, 317 Nishino, Numazu City, Shizuoka, 410-0395, Japan

来源：

Journal of Alloys and Compounds | 2007年 / 439卷 / 1-2期

关键词：

In this work; the TiFe single phase alloy with CsCl-type structure was synthesized after 20 h of ball milling (mechanical alloying). Alloying process of mixture of Ti and Fe powders to the TiFe phase was discussed. It was found that synthesis of the CsCl-type TiFe phase followed the amorphous phase formation. Hydrogenation properties of obtained TiFe alloy were studied. It was found that the hydrogenation properties of TiFe synthesized by mechanical alloying were different from those of previously reported. The first plateau pressure was found at 0.5 MPa which is slightly higher than the value previously reported. However; the second plateau pressure was found at 25 MPa; which is much higher than the literature value. The maximum amount of hydrogen absorbed in the TiFe alloy was about 1.3 wt.% at 298 K. © 2006 Elsevier B.V. All rights reserved;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

页码：221 / 226

共 50 条

[21] Compositional effects on the mechanochemical synthesis of Fe-Ti and Cu-Ti amorphous alloys by mechanical alloying
Delogu, F
Cocco, G
JOURNAL OF ALLOYS AND COMPOUNDS, 2003, 352 (1-2) : 92 - 98
[22] Effect of cooling process on the α phase formation and mechanical properties of sintered Ti-Fe alloys
Chen, Bor-Yuan
Hwang, Kuen-Shyang
Ng, Ka-Lok
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (13-14): : 4556 - 4563
[23] Wear resistance of cast dental Ti-Fe alloys
Yamaguchi, Hirofumi
Takahashi, Masatoshi
Sasaki, Keiichi
Takada, Yukyo
DENTAL MATERIALS JOURNAL, 2021, 40 (01) : 68 - 73
[24] Mssbauer Study of Mechanical Alloying Fe-Ti and Fe-Ti-N Alloys
Journal of Materials Science & Technology, 2001, (01) : 1 - 2
[25] Laser-induced self-propagating reaction synthesis of Ti-Fe alloys
Wang, C. S.
Zhang, K. S.
Pang, H. J.
Chen, Y. Z.
Dong, C.
JOURNAL OF MATERIALS SCIENCE, 2008, 43 (01) : 218 - 221
[26] MECHANICAL ALLOYING OF TI-ALLOYS
NASH, P
JOURNAL OF METALS, 1987, 39 (07): : A24 - A24
[27] On the influence of the heat treatment on microstructure formation and mechanical properties of near-α Ti-Fe alloys
Sandloebes, Stefanie
Korte-Kerzel, Sandra
Raabe, Dierk
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 748 : 301 - 312
[28] Mechanical grinding of rapidly solidified Ti-Fe alloy
Kobayashi, Keizo
Matsumoto, Akihiro
Ozaki, Kimihiro
Sugiyama, Akira
Honda, Yoshihiko
Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy, 2000, 47 (06): : 636 - 640
[29] Sintered Ti-Fe alloys with in situ synthesized TiC dispersoids
Chen, Bor-Yuan
Hwang, Kuen-Shyang
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 541 : 88 - 97
[30] Characteristic properties of Hot Isostatically Pressed Ti-Fe alloys
Kazuhiko, Majima, 1600, (36):

← 1 2 3 4 5 →