Fatigue analysis of crack growing rate and stress intensity factor for stress corrosion cracking in a pipeline system

被引：0
|
作者：
Shahani, A.R. [1 ]
Mahdavi, E. [1 ]
Amidpour, M. [1 ]
机构：
[1] Department of Mechanical Engineering, K. N. Toosi University of Technology, Tehran, Iran
来源：
World Academy of Science, Engineering and Technology | 2009年 / 33卷
关键词：
Brittle fracture - Stress corrosion cracking - Offshore structures - Fatigue crack propagation - Hydrogen embrittlement - Pipelines - Corrosion fatigue - Pipeline corrosion - Hydrogen;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：785 / 788
相关论文
共 50 条
  • [41] A CONSIDERATION OF EVALUATION OF FATIGUE-CRACK PROPAGATION RATE FROM EFFECTIVE STRESS INTENSITY FACTOR RANGE
    MAKABE, C
    KANESHIRO, H
    NISHIDA, S
    SAKIHAMA, H
    JOURNAL OF TESTING AND EVALUATION, 1995, 23 (03) : 153 - 159
  • [42] CONTROL OF PIPELINE STRESS-CORROSION CRACKING IS PROBED
    ALMQUIST, WE
    OIL & GAS JOURNAL, 1979, 77 (43) : 69 - 73
  • [43] THRESHOLD STRESS INTENSITY FOR STRESS CORROSION CRACK GROWTH.
    Smith, E.
    Res Mechanica: International Journal of Structural Mechanics and Materials Science, 1982, 4 (02): : 151 - 157
  • [44] Monitoring stress corrosion cracking in a working gas pipeline
    Khoroshikh, AV
    Kremlev, VV
    Surkov, YP
    Rybalko, VG
    Vaulin, SL
    RUSSIAN JOURNAL OF NONDESTRUCTIVE TESTING, 1999, 35 (07) : 517 - 522
  • [45] Detection of fatigue crack initiated at weld toe and evaluation of stress intensity factor range by means of thermoelastic stress analysis
    Honda, Takashi
    Sasaki, Tetsuya
    Yamaguchi, Atsushi
    Yoshihisa, Etsuji
    Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 2007, 73 (11): : 1280 - 1287
  • [46] Effect of strain rate on stress corrosion cracking of X80 pipeline steel
    Cheng, Y. (chengyuan621@sina.com), 1600, Beijing Institute of Aeronautical Materials (BIAM)
  • [47] Determination of stress intensity factor for mode I fatigue crack based on finite element analysis
    Han, Qinghua
    Wang, Yaru
    Yin, Yue
    Wang, Danni
    ENGINEERING FRACTURE MECHANICS, 2015, 138 : 118 - 126
  • [48] Determination of threshold stress intensity factor for stress corrosion cracking (KISCC) of steel heat affected zone
    Pal, Sarvesh
    Raman, R. K. Singh
    CORROSION SCIENCE, 2009, 51 (10) : 2443 - 2449
  • [49] THE INFLUENCE OF THE STRESS INTENSITY FACTOR ON THE FRACTOGRAPHY OF STRESS-CORROSION CRACKING OF 316 STAINLESS-STEEL
    LI, SQ
    DICKSON, JI
    BAILON, JP
    TROMANS, D
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 119 : 59 - 72
  • [50] Film rupture model for aqueous stress corrosion cracking under constant and variable stress intensity factor
    Hall, M. M., Jr.
    CORROSION SCIENCE, 2009, 51 (02) : 225 - 233
12345