Raman spectra and room-temperature ferromagnetism of hydrogenated Zn 0.95Mn0.05O nanopowders

被引：0
|
作者：
Wang, Zhenhua [1 ]
Geng, Dianyu [1 ]
Hu, Weijin [1 ]
Zhang, Zhidong [1 ]
机构：
[1] Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Road, Shenyang 110016, China
来源：
Journal of Applied Physics | 2009年 / 105卷 / 12期
关键词：
Two additional vibration modes at 250 and 529 cm-1 were observed in hydrogenated Zn0.98Mn0.05O nanopowders. The number of oxygen vacancies was increased by hydrogenation; which induced the mode at 250 cm-1. The additional vibration mode at 529 cm-1 was due to the increase of the number of subsititutional Mn atoms occupying Zn sites; which resulted that some new lattice defects were introduced or intrinsic host-lattice defects became activated/intensified. The room-temperature ferromagnetism was observed in the hydrogenated Zn0.98Mn0.05O nanopowders prepared at high temperature (T=700 °C); which originated from the lattice defects such as oxygen vacancies and Zn interstitials. © 2009 American Institute of Physics;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Conference article (CA)
引用
收藏
相关论文
共 50 条
  • [41] Enhancement of ferromagnetism in Zn0.95Co0.05O films by lithium codoping
    Li, Jian-jun
    Hao, Wei-chang
    Xu, Huai-zhe
    Wang, Tian-min
    Shi, Ji
    JOURNAL OF APPLIED PHYSICS, 2009, 106 (06)
  • [42] Room-temperature electroluminescence in the InAsSbP/InAs0.95Sb0.05/ 0.95 Sb 0.05 / InAsSbP single quantum well
    Moiseev, K. D.
    Ivanov, E. V.
    Romanov, V. V.
    JOURNAL OF LUMINESCENCE, 2024, 276
  • [43] Room-temperature ferromagnetism in Mn-implanted amorphous Ge
    Ottaviano, L.
    Continenza, A.
    Profeta, G.
    Impellizzeri, G.
    Irrera, A.
    Gunnella, R.
    Kazakova, O.
    PHYSICAL REVIEW B, 2011, 83 (13):
  • [44] Site-Specific Hydrogen Reactivity of Zn0.05Mg0.95O Nanopowders
    Haque, Francia
    Finocchi, Fabio
    Jupille, Jacques
    Stankic, Slavica
    JOURNAL OF PHYSICAL CHEMISTRY C, 2021, 125 (46): : 25841 - 25850
  • [45] Room-temperature ferromagnetism of Zn0.97Co0.03O pressed nanocrystalline powders
    Hu, Jifan
    Qin, Hongwei
    Xue, Tianfeng
    Cao, Ensi
    Li, Dengtao
    APPLIED PHYSICS LETTERS, 2008, 93 (02)
  • [46] Surface of Zn-Mn-O and its role in room temperature ferromagnetism: An XPS analysis
    Milivojevic, Dusan
    Babic-Stojic, Branka
    Kovac, Janez
    APPLIED SURFACE SCIENCE, 2010, 257 (03) : 937 - 943
  • [47] Fabrication of vertically well-aligned (Zn,Mn)O nanorods with room temperature ferromagnetism
    Baik, JM
    Lee, JL
    ADVANCED MATERIALS, 2005, 17 (22) : 2745 - +
  • [48] Room-temperature ferromagnetism in self-assembled (In, Mn)As quantum dots
    Chen, Y. F.
    Huang, J. H.
    Lee, W. N.
    Chin, T. S.
    Huang, R. T.
    Chen, F. R.
    Kai, J. J.
    Ku, H. C.
    APPLIED PHYSICS LETTERS, 2007, 90 (02)
  • [49] Room-temperature ferromagnetism of Mn-doped InAs by a diffusion treatment
    Dong, Shan
    Zhu, Feng
    Yang, Guandong
    OPTOELECTRONICS AND ADVANCED MATERIALS-RAPID COMMUNICATIONS, 2012, 6 (1-2): : 174 - 177
  • [50] Room-temperature ferromagnetism in Mn-implanted TiO2
    Menzel, D.
    Jursic, I.
    Schoenes, J.
    Iacomi, F.
    Cacaina, D.
    PHYSICA STATUS SOLIDI C - CURRENT TOPICS IN SOLID STATE PHYSICS, VOL 3, NO 12, 2006, 3 (12): : 4119 - 4122
12345