Natural Aging Behaviour of the EN AW 6082 and Lead Free EN AW 6023 Aluminium Alloys

被引：0
|
作者：
Fujda M. [1 ]
Matvija M. [1 ]
Glogovský M. [1 ]
Orišenko I. [1 ]
机构：
[1] Faculty of Materials, Metallurgy and Recycling, Technical University of Kosice, Letna 9, Kosice
来源：
Manufacturing Technology | 2017年 / 17卷 / 05期
关键词：
AlMgSi alloy; Mechanical properties; Microstructure; Natural aging; Sn;
D O I：
10.21062/ujep/x.2017/a/1213-2489/MT/17/5/701
中图分类号：
学科分类号：
摘要：
The natural aging behaviour of EN AW 6082 aluminium alloy and lead-free EN AW 6023 aluminium alloy with good free cutting machinability was investigated using Vickers microhardness measurements, tensile test analysis, and a light microscopy characterisation. The different chemical composition of the analysed alloys did not affect the alloys microhardness after quenching, but the solid solution grain sizes of the quenched alloys differed greatly. The microhardness and tensile strength of EN AW 6082 increased with aging time right after alloy quenching. On the contrary, microhardness and tensile strength of lead-free EN AW 6023 increased markedly until after 500 hours of natural aging. The natural aging of the 6023 alloy could be suppressed by the formation of Sn-vacancy pairs after alloy quenching that impede the strengthening clusters formation. Finer grains of solid solution that were found in the 6023 alloy microstructure resulted in higher tensile strength and lower ductility of the 6023 alloy compared to the 6082 alloy, even though the microhardness of the naturally aged 6023 alloy state was lower. © 2017 Copyright © 2017. Published by Manufacturing Technology. All rights reserved. All Rights Reserved.
引用
收藏
页码：19 / 20
页数：1
相关论文
共 50 条
  • [31] The Influence of Silicon in EN AW 6082 Alloys on the Bond Strength in Cold Pressure Welding
    Gerlitzky, Christiane
    Arbo, Siri Marthe
    Westermann, Ida
    Groche, Peter
    PROCEEDINGS OF THE 22ND INTERNATIONAL ESAFORM CONFERENCE ON MATERIAL FORMING (ESAFORM 2019), 2019, 2113
  • [32] Influence of rotary swaging and subsequent age hardening on properties of EN AW 6082 aluminium alloy
    Malecek, L.
    Palan, J.
    Nachazel, J.
    Dlouhy, J.
    4TH INTERNATIONAL CONFERENCE RECENT TRENDS IN STRUCTURAL MATERIALS, 2017, 179
  • [33] STUDY OF THE HIGH-TEMPERATURE BEHAVIOUR OF ALUMINIUM ALLOY EN AW 2014
    Bidulska, J.
    Pokorny, I.
    Kvackaj, T.
    Bidulsky, R.
    Grande, M. Actis
    ARCHIVES OF METALLURGY AND MATERIALS, 2011, 56 (04) : 981 - 989
  • [34] Behaviour of Aluminium EN AW 6082 T6 Columns Exposed to Transient Heating-Experimental and Numerical Analysis
    Goreta, Marko
    Toric, Neno
    Boko, Ivica
    Divic, Vladimir
    METALS, 2022, 12 (08)
  • [35] Small fatigue crack growth in aluminium alloy EN-AW 6082/T6
    Jisa, D.
    Liskutin, P.
    Kruml, T.
    Polak, J.
    INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (12) : 1913 - 1920
  • [36] MECHANICAL AND CORROSION PROPERTIES OF ALUMINIUM ALLOY EN AW 6082 AFTER SEVERE PLASTIC DEFORMATION (SPD)
    Lackova, P.
    Bursak, M.
    Kvackaj, T.
    Halama, M.
    METALURGIJA, 2015, 54 (01): : 181 - 183
  • [37] Low energy versus pulse in MIG welding of thin sheets of aluminium alloy EN AW 6082
    Adamiec, Janusz
    Rykala, Janusz
    Solid State Phenomena, 2015, 229 : 35 - 44
  • [38] Preparation and Etching Methods for a Light-Optical Microscopy Analysis of Extrusion Seams and Microstructural Contrasting for Aluminum Alloys EN AW-6063 and EN AW-6082
    Reeb, A.
    Ohl, A.
    Poser, K.
    Kloppenborg, T.
    Brosius, A.
    Tekkaya, A. E.
    Weidenmann, K. A.
    PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY, 2012, 49 (10): : 612 - 622
  • [39] Ultra fine structure and properties formation of en AW 6082 alloy
    Faculty of Metallurgy, Technical University of Košice, Letná9, Slovakia
    不详
    High Temp Mater Processes, 2008, 3 (193-202):
  • [40] The Effect of Homogenization Parameters on the Structure of EN AW-6082 Alloy
    Luštinec J.
    Očenášek V.
    Jelínek M., jr.
    Manufacturing Technology, 2017, 17 (05): : 41
12345