Study of the formation and thermal stability of Mg2Co obtained by mechanical alloying and heat treatment

被引：0
|
作者：
机构：
[1] [1,Martínez, Carola
[2] Ordoñez, Stella
[3] Serafini, Daniel
[4] Guzmán, Danny
[5] Rojas, Paula
来源：
Martínez, C. (carola.martinezu@usach.cl) | 1600年 / Elsevier Ltd卷 / 590期
关键词：
The microstructural evolution of Mg and Co in a 2:1 atomic ratio was investigated during mechanical alloying and subsequent heat treatments. Microstructural characterization was determined using X-ray diffraction and scanning electron microscopy; while thermal stability was studied by means of differential scanning calorimetry. The results show that mechanical alloying produces amorphization and promotes greater microstructural refinement. Formation of Mg2Co requires an additional heat treatment at temperatures between 679 and 705 K; depending on milling time. Additionally; it was determined that the activation energy for Mg2Co crystallization decreases from 206 to 184 kJ/mol when the milling time increases from 12 to 36 h; respectively; Finally; a combination of the mechanical alloying process and heat treatment phase evolutions was proposed as an optimal processing route in order to obtain the Mg2Co compound. © 2013 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [21] Synthesis and characterization of nanocrystalline Mg2CoH5 obtained by mechanical alloying
    J. Chen
    H. T. Takeshita
    D. Chartouni
    N. Kuriyama
    T. Sakai
    Journal of Materials Science, 2001, 36 : 5829 - 5834
  • [22] Synthesis and characterization of nanocrystalline Mg2CoH5 obtained by mechanical alloying
    Chen, J
    Takeshita, HT
    Chartouni, D
    Kuriyama, N
    Sakai, T
    JOURNAL OF MATERIALS SCIENCE, 2001, 36 (24) : 5829 - 5834
  • [23] Mechanical alloying and thermal treatment of the Fe-Co-Ag system
    González, G
    Sagarzazu, A
    Villalba, R
    Ochoa, J
    ISMANAM 2003: METASTABLE, MECHANICALLY ALLOYED AND NANOCRYSTALLINE MATERIALS, 2004, 20-21 : 219 - 224
  • [24] In-situ formation of V and Mg2Co/Mg2CoH5 for boosting the hydrogen storage properties of MgH2
    Wang, Yazhou
    Wu, Jiaao
    Wang, Shunxiang
    Bai, Zixiang
    Xia, Yongpeng
    Xiang, Cuili
    Zou, Yongjin
    Xu, Fen
    Sun, Lixian
    Chua, Yong Shen
    Journal of Alloys and Compounds, 2024, 1008
  • [25] In-situ formation of V and Mg2Co/Mg2CoH5 for boosting the hydrogen storage properties of MgH2
    Wang, Yazhou
    Wu, Jiaao
    Wang, Shunxiang
    Bai, Zixiang
    Xia, Yongpeng
    Xiang, Cuili
    Zou, Yongjin
    Xu, Fen
    Sun, Lixian
    Chua, Yong Shen
    JOURNAL OF ALLOYS AND COMPOUNDS, 2024, 1008
  • [26] Hydrogen sorption properties of the nanocomposites Mg-Mg2Ni1-xCox obtained by mechanical alloying
    Khrussanova, M
    Grigorova, E
    Bobet, JL
    Khristov, M
    Peshev, P
    JOURNAL OF ALLOYS AND COMPOUNDS, 2004, 365 (1-2) : 308 - 313
  • [27] Thermal stability of amorphous Mg50Ni50 alloy produced by mechanical alloying
    Guzman, D.
    Ordonez, S.
    Serafini, D.
    Rojas, P. A.
    Aguilar, C.
    Santander, M.
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2010, 356 (02) : 120 - 123
  • [28] Preparation of Mg2Ni base alloy by the combination of mechanical alloying and heat treatment at low temperature
    Aymard, L
    Ichitsubo, M
    Uchida, K
    Sekreta, E
    Ikazaki, F
    JOURNAL OF ALLOYS AND COMPOUNDS, 1997, 259 (1-2) : L5 - L8
  • [29] Synthesis of Mg-Cu-Gd amorphous alloy by mechanical alloying and its thermal stability
    许春霞
    潘复生
    王敬丰
    汤爱涛
    胡耀波
    Transactions of Nonferrous Metals Society of China, 2006, (S3) : 1848 - 1850
  • [30] Synthesis of Mg-Cu-Gd amorphous alloy by mechanical alloying and its thermal stability
    Xu Chun-xia
    Pan Fu-sheng
    Wang Jing-feng
    Tang Ai-tao
    Hu Yao-bo
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2006, 16 : S1848 - S1850
12345