High-temperature oxidation resistance of Ti-45Al-8 (Nb, Hf, Y)-0.2B alloys

被引：0
|
作者：
Wang, Yanjing [1 ]
Li, Fei [1 ]
Gu, Yanpeng [1 ]
Wang, Jijie [1 ]
Du, Xinghao [1 ]
机构：
[1] Shenyang Aerospace University, Shenyang,110136, China
来源：
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering | 2016年 / 45卷 / 01期
关键词：
Three kinds of alloys were designed by making the niobium equivalent of 8 at% approximately; and the compositions of the alloys were Ti-45Al-8Nb-0.2B; Ti-45Al-7Nb-0.1Hf-0.1Y-0.2B as well as Ti-45Al-4Nb-0.5Hf-0.1Y-0.2B (at%). The interrupted oxidation behaviors of alloys at 900℃ in static air were studied. The results show that combined addition of Hf and Y can enhance adherence between the oxide film and the substrate; Ti-45Al-4Nb-0.5Hf-0.1Y-0.2B alloy with the low Nb/Hf ratio has a lower oxidation gain and strong oxidation resistance. Ti-45Al-7Nb-0.1Hf-0.1Y-0.2B alloy with the high Nb/Hf ratio has a higher oxidation gain and poor oxidation resistance. Oxidized samples were examined by scanning electron microscopy (SEM); energy dispersive X-ray analysis (EDX) and X-ray diffraction analysis (XRD). It is found that combined addition of Hf and Y can promote the whisker growth of Al2O3 oxide scale; which improves adherence of the oxide film; a large number of continuous and compact Al2O3 oxide scale has been found in the alloys with low Nb/Hf ratio; which improves oxidation resistance of the alloy; external oxidation in the alloy with high Nb/Hf ratio results in higher oxidation gain and poor oxidation resistance. © 2016; Science Press. All right reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：132 / 136
相关论文
共 50 条
  • [31] Oxidation behavior of Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2C-MxC(M=Ti,Zr,Hf,Nb,Ta) composite ceramic at high temperature
    徐帅
    王韬
    王新刚
    吴璐
    方忠强
    葛芳芳
    蒙萱
    廖庆
    魏金春
    李炳生
    Chinese Physics B, 2023, (06) : 726 - 734
  • [32] Fatigue Failure Analyses on a Ti-45Al-8Nb-0.2W-0.2B-0.1Y Alloy at Different Temperatures
    Wang, Xi-Shu
    Zhang, Min
    Song, Xi-Ping
    Jia, Su
    Chen, Qiang
    Kawagoishi, Norio
    MATERIALS, 2012, 5 (11): : 2280 - 2291
  • [33] Oxidation resistance of powder metallurgy Ti-45Al-10Nb alloy at high temperature
    Jin, Xuchen
    Ye, Peihao
    Ji, Hongrui
    Suo, Zhuanxia
    Wei, Boxin
    Li, Xuewen
    Fang, Wenbin
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2022, 29 (12) : 2232 - 2240
  • [34] Oxidation behavior of Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2C-Mx C (M = Ti, Zr, Hf, Nb, Ta) composite ceramic at high temperature
    Xu, Shuai
    Wang, Tao
    Wang, Xingang
    Wu, Lu
    Fang, Zhongqiang
    Ge, Fangfang
    Meng, Xuan
    Liao, Qing
    Wei, Jinchun
    Li, Bingsheng
    CHINESE PHYSICS B, 2023, 32 (06)
  • [35] COMPETITIVE EFFECT OF NB AND V ON HIGH-TEMPERATURE OXIDATION OF α2-TI-30AL ALLOYS
    Jullian, Domingo
    Hayashi, Shigenari
    Takeyama, Masao
    JOINT EPRI - 123HIMAT INTERNATIONAL CONFERENCE ON ADVANCES IN HIGH-TEMPERATURE MATERIALS, 2019, 2019, : 971 - 975
  • [36] Improvement in the oxidation resistance of Nb-Ti-Si-Cr-Al-Hf alloys containing alloyed Ge and B
    Su, Linfen
    Jia, Lina
    Weng, Junfei
    Hong, Zhen
    Zhou, Chungen
    Zhang, Hu
    CORROSION SCIENCE, 2014, 88 : 460 - 465
  • [37] Characteristics of the Dynamic Recrystallization Behavior of Ti-45Al-8.5Nb-0.2W-0.2B-0.3Y Alloy during High Temperature Deformation
    Xiang, Lin
    Tang, Bin
    Xue, Xiangyi
    Kou, Hongchao
    Li, Jinshan
    METALS, 2017, 7 (07):
  • [38] Microstructures and mechanical properties of directionally solidified Ti-45Al-8Nb-(W, B, Y) alloys
    Ding, X. F.
    Lin, J. P.
    Zhang, L. Q.
    Song, X. P.
    Chen, G. L.
    MATERIALS & DESIGN, 2011, 32 (01) : 395 - 400
  • [39] Constitutive modeling of high temperature flow behavior in a Ti-45Al-8Nb-2Cr-2Mn-0.2Y alloy
    Gengwu Ge
    Laiqi Zhang
    Jingjing Xin
    Junpin Lin
    Mark Aindow
    Lichun Zhang
    Scientific Reports, 8
  • [40] Constitutive modeling of high temperature flow behavior in a Ti-45Al-8Nb-2Cr-2Mn-0.2Y alloy
    Ge, Gengwu
    Zhang, Laiqi
    Xin, Jingjing
    Lin, Junpin
    Aindow, Mark
    Zhang, Lichun
    SCIENTIFIC REPORTS, 2018, 8
12345