Evaluation of static and fatigue strength characteristics for thermal sprayed WC-Co materials by indentation method

被引：0

作者：

Nakanishi K. ^{[1
]}

Sakaue K. ^{[1
]}

Ogawa T. ^{[1
]}

Kobayashi Y. ^{[1
]}

机构：

[1] Department of Mechanical Engineering, Aoyama Gakuin University, Chuou-ku, Sagamihara-shi, Kanagawa, 252-5258

来源：

Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A | 2010年 / 76卷 / 767期

关键词：

Anisotropy; Brittle fracture; Coating material; Fatigue; HVOF; Indentation;

D O I：

10.1299/kikaia.76.902

中图分类号：

学科分类号：

摘要：

Static and cyclic indentation tests were performed on the surface and the cross-section of thermal sprayed WC-Co materials. Micro indentation tests revealed that the mechanical properties on the surface are different from those on the cross-section. Also, the static strength on the surface is lower than that on the cross section. Under the static indentation tests, the cracks on the surface formed a ring crack around the impression. On the other hand, the crack on the cross-section grew in the direction perpendicular to the sprayed direction. The results of cyclic indentation tests showed that the cyclic number for the crack initiation decreased with increasing the maximum surface stress. The fatigue strength on the cross section was slightly higher than on the surface. These results mean that thermal-sprayed WC materials clearly have cyclic fatigue behavior and remarkable anisotropy.

引用

页码：902 / 907

页数：5

共 50 条

[41] On bending strength of superhard composite materials based on WC-Co hardmetals
Golovchan, V. T.
STRENGTH OF MATERIALS, 2009, 41 (06) : 603 - 612
[42] Corrosion Behavior of WC-Co Coatings With VC Additions Applied By Thermal Sprayed HVOF
Gutierrez, J. A.
Gaona, C.
Estupinan, F.
Zambrano, P.
Almeraya, F.
Cabral, J. A.
XXXII NATIONAL CONGRESS OF THE MEXICAN SOCIETY OF ELECTROCHEMISTRY/10TH MEETING OF THE ECS MEXICAN SECTION, 2018, 84 (01): : 67 - 76
[43] Damage tolerance and residual fatigue strength/life of WC-Co cemented carbides
Mahani, S. Fooladi
Liu, C.
Lin, L. L.
Ramirez, G.
Wen, X.
Llanes, L.
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2025, 129
[44] Analysis of thermal load and surface temperature in the production of thermally sprayed WC-Co coatings
Zhao, Min
Gadow, R.
Kirringer, A.
Cander-Ruiz, A.
Shenyang Jianzhu Daxue Xuebao (Ziran Kexue Ban)/Journal of Shenyang Jianzhu University (Natural Science), 2006, 22 (06): : 1052 - 1056
[45] Corrosion-wear behaviour of thermal sprayed nanostructured FeCu/WC-Co coatings
Basak, A. K.
Matteazzi, P.
Vardavoulias, M.
Celis, J. -P.
WEAR, 2006, 261 (09) : 1042 - 1050
[46] Effect of nanostructuring and Al alloying on corrosion behaviour of thermal sprayed WC-Co coatings
Basak, A. K.
Celis, J. -P.
Ponthiaux, P.
Wenger, F.
Vardavoulias, M.
Matteazzi, P.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 558 : 377 - 385
[47] Wear behaviour of HVOF thermal sprayed WC-Co and CrC-NiCr coatings
Forn, A
Picas, JA
Matthäus, G
THERMEC'2003, PTS 1-5, 2003, 426-4 : 2623 - 2628
[48] Microstructural characteristics of high-feed milled HVOF sprayed WC-Co coatings
Tillmann, Wolfgang
Hagen, Leif
Stangier, Dominic
Paulus, Michael
Tolan, Metin
Sakrowski, Robin
Biermann, Dirk
Freiburg, Dennis
SURFACE & COATINGS TECHNOLOGY, 2019, 374 : 448 - 459
[49] Effects of Particle Strength of Feedstock Powders on Properties of Warm-Sprayed WC-Co Coatings
Pornthep Chivavibul
Makoto Watanabe
Seiji Kuroda
Jin Kawakita
Masayuki Komatsu
Kazuto Sato
Junya Kitamura
Journal of Thermal Spray Technology, 2011, 20 : 1098 - 1109
[50] Evaluation of fatigue strength of WC cermet- and 13Cr steel-sprayed materials and their coatings
Ogawa, T
Tokaji, K
Ejima, T
Kobayashi, Y
Harada, Y
THERMAL SPRAY, VOLS 1 AND 2: MEETING THE CHALLENGES OF THE 21ST CENTURY, 1998, : 635 - 640

← 1 2 3 4 5 →