Preparation of PZT(95/5) antiferroelectric nanoscale powders using sol-gel method

被引：0
|
作者：
Yao, Hai-Yun [1 ]
Hu, Yan-Hua [1 ]
Yu, Zhan-Jun [1 ]
Wang, Li-Xia [2 ]
机构：
[1] Department of Materials, Inner Mongolia University of Technology, Hohhot, China
[2] Technology Department of Fucheng Forging Company, Inner Mongolia First Machinery Manufacturing, Baotou, China
来源：
Gongneng Cailiao/Journal of Functional Materials | 2014年 / 45卷
关键词：
Sol-gel process - Differential thermal analysis - Powders - Nanotechnology - Perovskite;
D O I：
10.3969/j.issn.1001-9731.2014.Suppl.(2).030
中图分类号：
学科分类号：
摘要：
PZT(95/5) antiferroelectric nanoscale powders were prepared by sol-gel process. 550-750, calcination temperature range of dried PZT(95/5) powder were identified by differential thermal analysis. Dried powders were calcinated at 550, 600, 650, 750, holding for 2 hours, respectively. XRD analysis showed that the strength of the main crystalline phase gradually increases, the impurity phase peak height decreases with the increasing of the calcination temperature. When calcinated at 750, single perovskite phase was formed and PZT95/5 powders size was about 100 nm. ©, 2014, Journal of Functional Materials. All right reserved.
引用
收藏
页码：140 / 143
相关论文
共 50 条
  • [41] Effect of acetylacetone on the preparation of PZT materials in sol-gel processing
    Weng, LQ
    Bao, XJ
    Sagoe-Crentsil, K
    MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY, 2002, 96 (03): : 307 - 312
  • [42] Optimization of processing parameters of PZT ceramic prepared by Sol-Gel Derived Nanocrystalline PZT Powders
    Mirzaee, Ali
    Barzegar, Abdolghaffar
    2009 9TH IEEE CONFERENCE ON NANOTECHNOLOGY (IEEE-NANO), 2009, : 317 - +
  • [43] Fabrication of Bi-2223 Powders Using Sol-Gel Method
    Li, Mingya
    Wang, Xiaoyan
    Ye, Chengli
    Xue, Fenglin
    CHINESE CERAMICS COMMUNICATIONS II, 2012, 412 : 125 - 128
  • [44] Preparation and characteristics of Nb5+, Ta5+/TiO2 nanoscale powders by sol-gel process using TiCl3
    Pan, HB
    Chen, NS
    Shen, SF
    Huang, JL
    JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2005, 34 (01) : 63 - 69
  • [45] Low temperature sintering of PZT powders coated with Pb5Ge3O11 by sol-gel method
    Hayashi, T
    Inoue, T
    Akiyama, Y
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 1999, 19 (6-7) : 999 - 1002
  • [46] Low-temperature processing and characterization of single-phase PZT powders by sol-gel method
    Radhouane Bel Hadj Tahar
    Noureddine Bel Hadj Tahar
    Abdelhamid Ben Salah
    Journal of Materials Science, 2007, 42 : 9801 - 9806
  • [47] Low-temperature processing and characterization of single-phase PZT powders by sol-gel method
    Tahar, Radhouane Bel Hadj
    Tahar, Noureddine Bel Hadj
    Ben Salah, Abdelhamid
    JOURNAL OF MATERIALS SCIENCE, 2007, 42 (23) : 9801 - 9806
  • [48] Influence of hydrolysis conditions of the acetate sol-gel process on the stoichiometry of PZT powders
    Bruncková, H
    Medvecky, L
    Briancin, J
    Saksl, K
    CERAMICS INTERNATIONAL, 2004, 30 (03) : 453 - 460
  • [49] Sol-gel preparation of PZT powders and its catalytic effect on burning rate of RDX-CMDB propellant
    Qin, Mingna
    Zheng, Xiaodong
    Yan, Qilong
    Yuan, Tiegang
    Tang, Wang
    Li, Hongli
    Qiu, Shaojun
    SCIENCE AND TECHNOLOGY OF ENERGETIC MATERIALS, 2012, 73 (3-4) : 88 - 92
  • [50] Preparation and fluorescence property of pure Bi2SiO5 powders by Pechini sol-gel method
    Wu, Yuanting
    Li, Menglong
    Wang, Xiufeng
    Wang, Lili
    Gao, Hui
    MATERIALS AND MANUFACTURING PROCESSES, 2017, 32 (05) : 480 - 483
12345