Effect of CrN coating on the hot salt corrosion fatigue behavior of titanium alloy

被引：0
|
作者：
Li, Rong-Zhi [1 ,2 ]
Cheng, Cong-Qian [1 ]
Pu, Ji-Bin [2 ]
Min, Xiao-Hua [1 ]
Cao, Tie-Shan [1 ]
Zhao, Jie [1 ]
机构：
[1] Dalian Univ Technol, Sch Mat Sci & Engn, Dalian 116024, Peoples R China
[2] Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Key Lab Marine Mat & Related Technol, Key Lab Marine Mat & Protect Technol Zhejiang Prov, Ningbo 315201, Peoples R China
来源：
CORROSION SCIENCE | 2024年 / 240卷
基金：
中国国家自然科学基金;
关键词：
CrN coating; Hot salt corrosion fatigue; Failure behavior; Titanium alloy; LOW-CYCLE FATIGUE; SOLID NACL DEPOSIT; MULTILAYER COATINGS; NACL-H2O-O-2; RESISTANCE;
D O I：
10.1016/j.corsci.2024.112448
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The dwell fatigue behavior of CrN coated titanium alloys were carried out in air and hot salt corrosive environment at 500 degree celsius. The results indicate that the decrease of the elastic modulus difference between the coating and the substrate alleviates the deformation mismatch issue at high temperature. Stress relaxation at the crack tip caused by Cr transition layer oxidation can improve the fatigue properties of the coated samples. Furthermore, the CrN coating enhances the corrosion fatigue properties, which is related to the barrier effect of the coating on the corrosive medium. The crack growth mode in the substrate transition from stress corrosion crack to fatigue damage crack.
引用
收藏
页数：13
相关论文
共 50 条
  • [41] EFFECT OF A TITANIUM COATING ON CORROSION FATIGUE-STRENGTH OF A HIGH-CHROME STEEL
    MARININ, VG
    KHOKHLOV, NI
    SOVIET MATERIALS SCIENCE, 1990, 26 (05): : 597 - 598
  • [42] Effect of titanium aluminide coating on cyclic plastic deformation and fatigue life of a titanium alloy at 600°C
    Sahu, J. K.
    Das, D. K.
    Nandy, T. K.
    Mandal, D.
    Rajinikanth, V.
    Swaminathan, J.
    Ray, A. K.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 530 : 664 - 668
  • [43] Effect of TiN monolithic and Ti/TiN multilayer coating on the fatigue behavior of titanium alloy under tension-tension
    Zhang, Zhaolu
    Yang, Minglei
    He, Guangyu
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 31 : 3675 - 3689
  • [44] Effect of titanium addition on the corrosion behavior of CoCuFeNiMn high entropy alloy
    Öztürk, Sultan
    Alptekin, Furkan
    Önal, Suat
    Sünbül, Sefa Emre
    Şahin, Ömer
    İçin, Kürşat
    Journal of Alloys and Compounds, 2022, 903
  • [45] Effect of hydroxyapatite-titanium-MWCNTs composite coating fabricated by electrophoretic deposition on corrosion and cellular behavior of NiTi alloy
    Maleki-Ghaleh, Hossein
    Khalil-Allafi, Jafar
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2019, 70 (11): : 2128 - 2138
  • [46] Effect of titanium addition on the corrosion behavior of CoCuFeNiMn high entropy alloy
    Ozturk, Sultan
    Alptekin, Furkan
    Onal, Suat
    Sunbul, Sefa Emre
    Sahin, Omer
    Icin, Kursat
    JOURNAL OF ALLOYS AND COMPOUNDS, 2022, 903
  • [47] Environmental effect of hot corrosion on creep and fatigue failure of thermal barrier coating systems
    Takahashi, Satoru
    Yoshiba, Masayuki
    Kakuta, Wataru
    Matsuoka, Sayuri
    Harada, Yoshio
    HIGH-TEMPERATURE OXIDATION AND CORROSION 2005, 2006, 522-523 : 353 - 359
  • [48] The Effect of Hot Corrosion and Electrochemical Corrosion on Microhardness of the Coating
    Arpit R. Patil
    S. T. Vagge
    High Temperature Corrosion of Materials, 2024, 101 : 471 - 483
  • [49] The Effect of Hot Corrosion and Electrochemical Corrosion on Microhardness of the Coating
    Patil, Arpit R.
    Vagge, S. T.
    HIGH TEMPERATURE CORROSION OF MATERIALS, 2024, 101 (03) : 471 - 483
  • [50] EFFECT OF MICROSTRUCTURE ON HOT SALT STRESS-CORROSION SUSCEPTIBILITY OF TITANIUM-ALLOYS
    MAHONEY, MW
    TETELMAN, AS
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1976, 7 (10): : 1549 - 1558
12345