Effect of CrN coating on the hot salt corrosion fatigue behavior of titanium alloy

被引：0
|
作者：
Li, Rong-Zhi [1 ,2 ]
Cheng, Cong-Qian [1 ]
Pu, Ji-Bin [2 ]
Min, Xiao-Hua [1 ]
Cao, Tie-Shan [1 ]
Zhao, Jie [1 ]
机构：
[1] Dalian Univ Technol, Sch Mat Sci & Engn, Dalian 116024, Peoples R China
[2] Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Key Lab Marine Mat & Related Technol, Key Lab Marine Mat & Protect Technol Zhejiang Prov, Ningbo 315201, Peoples R China
来源：
CORROSION SCIENCE | 2024年 / 240卷
基金：
中国国家自然科学基金;
关键词：
CrN coating; Hot salt corrosion fatigue; Failure behavior; Titanium alloy; LOW-CYCLE FATIGUE; SOLID NACL DEPOSIT; MULTILAYER COATINGS; NACL-H2O-O-2; RESISTANCE;
D O I：
10.1016/j.corsci.2024.112448
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The dwell fatigue behavior of CrN coated titanium alloys were carried out in air and hot salt corrosive environment at 500 degree celsius. The results indicate that the decrease of the elastic modulus difference between the coating and the substrate alleviates the deformation mismatch issue at high temperature. Stress relaxation at the crack tip caused by Cr transition layer oxidation can improve the fatigue properties of the coated samples. Furthermore, the CrN coating enhances the corrosion fatigue properties, which is related to the barrier effect of the coating on the corrosive medium. The crack growth mode in the substrate transition from stress corrosion crack to fatigue damage crack.
引用
收藏
页数：13
相关论文
共 50 条
  • [21] Hot Corrosion Behavior of DZ125 Alloy in Molten Salt Environment
    Li Y.
    Li N.
    Dong F.
    Hou J.
    Feng J.
    Geng G.
    Xiyou Jinshu/Chinese Journal of Rare Metals, 2020, 44 (01): : 107 - 112
  • [22] Hot corrosion behavior of AlCuFeCr quasicrystalline coating on titanium alloy with the mixture of NaCl and Na2SO4 deposit
    Wang, Fengfeng
    Zhou, Chungen
    Gong, Shengkai
    Xu, Huibin
    2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 2313 - +
  • [23] Study of the oxidation behavior of CrN coating on Zr alloy in air
    Meng, Chuiyi
    Yang, Liu
    Wu, Yawen
    Tan, Jie
    Dang, Weian
    He, Xiujie
    Ma, Xianfeng
    JOURNAL OF NUCLEAR MATERIALS, 2019, 515 : 354 - 369
  • [24] EFFECT OF HEAT-TREATMENT ON THE FATIGUE AND CORROSION FATIGUE BEHAVIOR OF A CUNICR ALLOY
    HAHN, HN
    DUQUETTE, DJ
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1979, 10 (10): : 1453 - 1460
  • [25] Effects of interaction between hot exposure and hot salt exposure on hot salt stress corrosion behavior of Ti811 alloy
    Zhao, Yongqing
    Zhu, Kangying
    Li, Zuochen
    Wu, Qingzhi
    Quan, Guiyi
    Wang, Gao
    Wang, Weiqi
    Wang, Xiaochao
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 1998, 8 (02): : 218 - 222
  • [26] Effect of Content of Graphene on Corrosion Behavior of Micro-Arc Oxidation Coating on Titanium Alloy Drill Pipe
    Chen, Xiaowen
    Liao, Dandan
    Zhang, Defen
    Jiang, Xuan
    Zhao, Pengfei
    Xu, Ruosi
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2020, 15 (01): : 710 - 721
  • [27] Effect of Al-Zn Alloy Coating on Corrosion Fatigue Behavior of X80 Riser Steel
    Han, Zhongying
    Huang, Xiaoguang
    Yang, Zhicheng
    MATERIALS, 2019, 12 (09):
  • [28] HOT SALT CORROSION TEST PROCEDURES AND COATING EVALUATION
    SAUNDERS, SRJ
    NICHOLLS, JR
    THIN SOLID FILMS, 1984, 119 (03) : 247 - 269
  • [29] Fretting fatigue wear behavior of Cu-aL coating on titanium alloy substrate
    Lee, H.
    Mall, S.
    PROCEEDINGS OF THE ASME/STLE INTERNATIONAL JOINT TRIBOLOGY CONFERENCE, PTS A AND B, 2008, : 537 - 538
  • [30] HOT-SALT STRESS-CORROSION OF TITANIUM
    PETERSEN, VC
    JOURNAL OF METALS, 1971, 23 (04): : 40 - &
12345