RELATIONSHIPS BETWEEN FRACTURE PARAMETERS AND FRACTURE SURFACE-ROUGHNESS OF BRITTLE POLYMERS

被引:93
|
作者
ARAKAWA, K
TAKAHASHI, K
机构
[1] Research Institute for Applied Mechanics, Kyushu University, Kasuga-shi
关键词
D O I
10.1007/BF00018393
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Fracture parameters such as crack velocity a, stress intensity factor K(d) and a specific crack extension resistance R* were measured for Homalite-100, PMMA and epoxy in the course of fast crack propagation using a Cranz-Schardin type high speed camera. Fracture surface roughness lambda was evaluated as a function of crack length a so that it could be correlated with the fracture parameters above. The results showed that none of those parameters could be uniquely related to lambda. Instead, there was a good correlation between lambda and a product R* a.
引用
收藏
页码:103 / 114
页数:12
相关论文
共 50 条
  • [41] UTILIZATION OF AN OPTOELECTRONIC SIGNAL TO DETERMINE SURFACE-ROUGHNESS PARAMETERS
    ZOLOTYKH, BN
    MOROZOVA, ND
    SOLODOV, SE
    MEASUREMENT TECHNIQUES USSR, 1989, 32 (05): : 408 - 411
  • [42] Evaluation of surface roughness by various parameters .1. Relationships between several roughness parameters and tactile roughness
    Fujii, Y
    Yoshizane, M
    Okumura, S
    MOKUZAI GAKKAISHI, 1997, 43 (07): : 574 - 579
  • [43] A local surface roughness mapping method for post-failure interpretation of brittle fracture propagation
    Magsipoc, Earl
    Grasselli, Giovanni
    INTERNATIONAL JOURNAL OF ROCK MECHANICS AND MINING SCIENCES, 2023, 172
  • [44] EFFECT OF CENTRIFUGAL BALLING PARAMETERS ON CHARACTERISTICS OF SURFACE-ROUGHNESS
    TUBIELEW.K
    MECHANIK MIESIECZNIK NAUKOWO-TECHNICZNY, 1974, 47 (02): : 89 - 92
  • [45] INFLUENCE OF SURFACE-ROUGHNESS PARAMETERS ON ELASTOHYDRODYNAMIC FILM THICKNESS
    JANCZAK, KJ
    WISNIEWSKI, MR
    WEAR, 1987, 115 (1-2) : 75 - 82
  • [46] SPATIAL VARIATION OF PARAMETERS DESCRIBING SOIL SURFACE-ROUGHNESS
    LEHRSCH, GA
    WHISLER, FD
    ROMKENS, MJM
    SOIL SCIENCE SOCIETY OF AMERICA JOURNAL, 1988, 52 (02) : 311 - 319
  • [47] Damage mechanisms in the dynamic fracture of nominally brittle polymers
    Davy Dalmas
    Claudia Guerra
    Julien Scheibert
    Daniel Bonamy
    International Journal of Fracture, 2013, 184 : 93 - 111
  • [48] Fracture parameters of bamboo scrimber's transverse quasi-brittle fracture
    Xie P.
    Liu W.
    Hu Y.
    Meng X.
    Zhang H.
    Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica, 2020, 37 (06): : 1466 - 1475
  • [49] Damage mechanisms in the dynamic fracture of nominally brittle polymers
    Dalmas, Davy
    Guerra, Claudia
    Scheibert, Julien
    Bonamy, Daniel
    INTERNATIONAL JOURNAL OF FRACTURE, 2013, 184 (1-2) : 93 - 111
  • [50] Brittle fracture in associative polymers: the case of ionomer melts
    Shabbir, Aamir
    Huang, Qian
    Chen, Quan
    Colby, Ralph H.
    Alvarez, Nicolas J.
    Hassager, Ole
    SOFT MATTER, 2016, 12 (36) : 7606 - 7612