THE RELATION BETWEEN FILAMENT DIAMETER AND FRACTURE STRENGTH FOR ULTRA-HIGH-MODULUS POLYETHYLENE FIBERS

被引：39
|
作者：
AMORNSAKCHAI, T
CANSFIELD, DLM
JAWAD, SA
POLLARD, G
WARD, IM
机构：
[1] IRC in Polymer Science and Technology, University of Leeds, Leeds
来源：
JOURNAL OF MATERIALS SCIENCE | 1993年 / 28卷 / 06期
关键词：
D O I：
10.1007/BF00363369
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effect of filament diameter on the failure stress of polyethylene fibres has been studied using Weibull analysis. Both gel-spun and melt-spun fibres have been examined, so that differences might be observed for changes in draw ratio or modulus as well as molecular weight. It is concluded that the strength of high-modulus melt-spun fibres relates to the concentration of flaws and is significantly dependent on filament diameter. Conflicting results for gel-spun fibres are discussed in the light of the present investigation, and it is concluded that the mechanism of failure in these fibres is different from that of the melt-spun fibres.
引用
收藏
页码：1689 / 1698
页数：10
相关论文
共 50 条
  • [41] The breaking strength of ultra-high molecular weight polyethylene fibers
    Department of Chemistry, Coll. Environ. Sci. Forest., Stt. U., Syracuse, NY 13210, United States
    Polymer, 26 (7261-7274):
  • [42] LARGE DIAMETER HIGH-STRENGTH, HIGH MODULUS CARBON-FIBERS FROM POLYACETYLENES
    KRUTCHEN, CM
    FLOM, DG
    GOROWITZ, B
    ROBERTS, BW
    CARBON, 1973, 11 (06) : 687 - 687
  • [43] Surface modification of ultra high modulus polyethylene fibers by an atmospheric pressure plasma jet
    Wang, T.
    Wang, C.
    Qiu, Y.
    JOURNAL OF APPLIED POLYMER SCIENCE, 2008, 108 (01) : 25 - 33
  • [44] CONTROLLED INTERFACES OF ULTRA-HIGH MODULUS POLYETHYLENE AND ARAMID FIBERS FOR ADVANCED COMPOSITES
    GUTOWSKI, WS
    PANKEVICIUS, ER
    WU, DY
    INTERFACES II, 1995, 189- : 211 - 219
  • [45] High modulus and high strength PP nanocomposite filament
    Chatterjee, A
    Deopura, BL
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2006, 37 (05) : 813 - 817
  • [46] DEVELOPMENT OF ULTRA-HIGH-MODULUS GRAPHITE-EPOXY FOR MISSILE STRUCTURAL APPLICATIONS
    KOO, FH
    EXPERIMENTAL MECHANICS, 1979, 19 (05) : N49 - N49
  • [47] THE FRACTURE PROCESS OF ULTRAHIGH STRENGTH POLYETHYLENE FIBERS
    SMOOK, J
    HAMERSMA, W
    PENNINGS, AJ
    JOURNAL OF MATERIALS SCIENCE, 1984, 19 (04) : 1359 - 1373
  • [48] Regulating the dissolving system of ultra-high molecular weight polyethylene to enhance the high-strength and high-modulus properties of resultant fibers
    Wang, Yi
    Fu, Jiabin
    Song, Qingquan
    Yu, Junrong
    Wang, Yan
    Hu, Zuming
    JOURNAL OF APPLIED POLYMER SCIENCE, 2022, 139 (29)
  • [49] HIGH STRENGTH AND HIGH MODULUS CARBON FIBERS
    BACON, R
    SCHALAMO.WA
    CARBON, 1968, 6 (02) : 211 - &
  • [50] High strength and high modulus carbon fibers
    Chae, Han Gi
    Newcomb, Bradley A.
    Gulgunje, Prabhakar V.
    Liu, Yaodong
    Gupta, Kishor K.
    Kamath, Manjeshwar G.
    Lyons, Kevin M.
    Ghoshal, Sushanta
    Pramanik, Chandrani
    Giannuzzi, Lucille
    Sahin, Korhan
    Chasiotis, Ioannis
    Kumar, Satish
    CARBON, 2015, 93 : 81 - 87
12345