ISOTHERMAL MELT PROCESSING OF BI-2212 THICK-FILMS

被引：29
|
作者：
HOLESINGER, TG
PHILLIPS, DS
COULTER, JY
WILLIS, JO
PETERSON, DE
机构：
[1] Superconductivity Technology Center, Los Alamos National Laboratory, Los Alamos
来源：
PHYSICA C | 1995年 / 243卷 / 1-2期
关键词：
D O I：
10.1016/0921-4534(94)02455-3
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
An alternative melt-processing technique has been developed for the fabrication of Bi2Sr2CaCu2Oy (Bi-2212) thick films at temperatures over 100 degrees C lower than those employed in conventional Bi-2212 melt processing. Isothermal melt processing combines the melting and solidification steps at the same temperature [T.G. Holesinger et al., Appl. Phys. Lett. 63 (1993) 982]. This technique is possible due to the large drop in the solidus temperature with decreasing oxygen partial pressure. High-quality thick films were processed at temperatures as low as 770 degrees C. Such films were found to be well-textured, contain relatively few secondary phases, and possess critical current densities over 1 X 10(5) A/cm(2) at 4 K in self-field.
引用
收藏
页码：93 / 102
页数：10
相关论文
共 50 条
  • [41] The effect of alumina additions on the processing of Bi-2212 conductors
    Holesinger, T. G.
    Kennison, J. K.
    Miao, H.
    Meinesz, M.
    Marken, K. R.
    Hong, S.
    Campbell, S.
    ADVANCES IN CRYOGENIC ENGINEERING, VOL 52A & 52B, 2006, 824 : 683 - +
  • [42] Surface resistance of Bi-2212 films and influence of intergrowth
    Otsuka, J
    Yamamoto, O
    Sugihara, Y
    Senzaki, T
    Ohbayashi, K
    Inoue, M
    Fujimaki, A
    Hayakawa, H
    PHYSICA C, 2000, 331 (02): : 164 - 170
  • [43] Ag distribution in thick Bi-2212 floating zone textured rods
    Sotelo, A
    Mora, M
    Madre, MA
    Diez, JC
    Angurel, LA
    De la Fuente, GF
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2005, 25 (12) : 2947 - 2950
  • [44] Enhancement of critical current density and flux pinning in Bi-2212 thick films due to MgO addition
    Ni, BR
    Kiuchi, M
    Otabe, ES
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2003, 13 (02) : 3695 - 3698
  • [45] The intergranular and intragranular properties of Ag-clamped Bi-2212 thick films melt-solidified with and without Bi2Al4O9
    Noji, H
    Sato, R
    Saito, T
    Awaji, S
    Watanabe, K
    SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2002, 15 (01): : 67 - 71
  • [46] Magnetoresistive effects in Bi-2212 melt textured bulk with MgO additions
    Winton, B
    Ionescu, M
    Silver, T
    Dou, SX
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2005, 38 (14) : 2327 - 2331
  • [47] Isothermal melt processed Bi-2212/Ag tapes containing MgO and Al2O3 additions
    Vo, NV
    Holesinger, TG
    Baldonado, PS
    Hults, WL
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2000, 11 (01) : 81 - 88
  • [48] Isothermal melt processed Bi-2212/Ag tapes containing MgO and Al2O3 additions
    N. V. Vo
    T. G. Holesinger
    P. S. Baldonado
    W. L. Hults
    Journal of Materials Science: Materials in Electronics, 2000, 11 : 81 - 88
  • [49] Overpressure processing of Ag-sheathed Bi-2212 tapes
    Reeves, JL
    Polak, M
    Zhang, W
    Hellstrom, EE
    Babcock, SE
    Larbalestier, DC
    Inoue, N
    Okada, M
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 1997, 7 (02) : 1541 - 1543
  • [50] Bi-2212 phase formation process in multifilamentary Bi-2212/Ag wires and tapes
    Koizumi, T
    Hasegawa, T
    Nishioka, J
    Hikichi, Y
    Nakatsu, T
    Kumakura, H
    Kitaguchi, I
    Matsumoto, A
    Nagaya, S
    IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2005, 15 (02) : 2538 - 2541
12345