EFFECT OF ION-BEAM MIXING TEMPERATURE ON COBALT SILICIDE FORMATION

被引：6

作者：

KASKO, I ^{[1
]}

DEHM, C ^{[1
]}

FREY, L ^{[1
]}

RYSSEL, H ^{[1
]}

机构：

[1] UNIV ERLANGEN NURNBERG,LEHRSTUHL ELEKTR BAUELEMENTE,W-8520 ERLANGEN,GERMANY

来源：

NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS | 1993年 / 80-1卷

关键词：

D O I：

10.1016/0168-583X(93)90682-V

中图分类号：

TH7 [仪器、仪表];

学科分类号：

0804 ; 080401 ; 081102 ;

摘要：

In this study, the influence of ion-beam mixing temperature on CoSi2 formation during subsequent annealing was investigated. For mixing of cobalt layers on silicon, germanium ions were implanted at various substrate temperatures ranging from 25 to 500-degrees-C. RBS and TEM investigations showed that only in the case of mixing temperatures at or above 400-degrees-C, silicide phases like Co2Si, CoSi, and CoSi2 were formed during mixing. Annealing at 700-degrees-C resulted in a complete conversion into CoSi2 for samples mixed at 400 and 500-degrees-C whereas no reaction could be observed for all other samples. A second annealing step at 1000-degrees-C was necessary to achieve complete silicidation also for these samples. However, only ion-beam mixing at 400 and 500-degrees-C led to uniform CoSi2 layers with abrupt silicide-silicon interfaces. It can be concluded that radiation enhanced reaction takes place when performing ion-beam mixing above a critical temperature. In this case, a sufficient metal amount could be mixed into the silicon surface resulting in uniform silicide growth.

引用

页码：786 / 789

页数：4

共 50 条

[21] TERNARY IRON-COBALT SILICIDE FABRICATED BY ION-BEAM SYNTHESIS
HARRY, MA
CURELLO, G
REESON, KJ
FINNEY, MS
HUTCHINSON, SV
GWILLIAM, RM
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1995, 96 (1-2): : 356 - 360
[22] ION-BEAM MIXING OF METALS AND DEBYE TEMPERATURE
IBRAHIM, AM
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1988, 34 (01): : 135 - 136
[23] RECENT PROGRESS IN REFRACTORY-METAL SILICIDE FORMATION BY ION-BEAM MIXING AND ITS APPLICATIONS TO VLSI
OKABAYASHI, H
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1989, 39 (1-4): : 246 - 252
[24] ORIGIN OF ION-BEAM MIXING EFFECTS ON MORPHOLOGICAL FEATURES IN SOLID-PHASE TITANIUM SILICIDE FORMATION
SUZUKI, T
MIYAZAKI, T
NATSUAKI, N
APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 1990, 50 (03): : 265 - 267
[25] THE EFFECT OF TEMPERATURE ON ION-BEAM MIXING OF MO FILMS ON SI SUBSTRATES
GAO, WY
LI, HC
WANG, RL
LIU, JR
VACUUM, 1989, 39 (2-4) : 259 - 261
[26] COMPUTER-SIMULATION OF ION-BEAM MIXING OF COBALT ON SILICON
CHAKAROV, IR
KARPUZOV, DS
EPM 87: ENERGY PULSE AND PARTICLE BEAM MODIFICATION OF MATERIALS, 1988, 8 : 357 - 359
[27] MODEL FOR COMPOUND FORMATION DURING ION-BEAM MIXING
DESIMONI, J
TRAVERSE, A
PHYSICAL REVIEW B, 1993, 48 (18): : 13266 - 13272
[28] PREDICTION OF AMORPHOUS ALLOY FORMATION BY ION-BEAM MIXING
ALONSO, JA
SIMOZAR, S
SOLID STATE COMMUNICATIONS, 1983, 48 (09) : 765 - 767
[29] ALUMINIDES AND SILICIDES FORMATION BY ION-BEAM MIXING OF MULTILAYERS
BAUMVOL, IJR
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1993, 74 (1-2): : 98 - 104
[30] FORMATION OF FERROMAGNETIC MNAL LAYERS BY ION-BEAM MIXING
KIDO, Y
SUZUKI, N
KAWAMOTO, J
JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1987, 26 (11): : L1900 - L1902

← 1 2 3 4 5 →