EDGE CREEP OF PREPAINTED ZN-55-PERCENT-AL COATED STEEL SHEET

被引：3
|
作者：
OKA, J
TAKASUGI, M
机构：
[1] Nippon Steel Corp, Japan
来源：
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN | 1991年 / 77卷 / 07期
关键词：
EDGE CREEP; PREPAINTED GALVALUME; ZN-AL ALLOY COATING; CORROSION; ATMOSPHERIC EXPOSURE TEST; PRETREATMENT; COATING;
D O I：
10.2355/tetsutohagane1955.77.7_1130
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The effects of pretreatments and paint coatings on the edge creep performance of prepainted Galvalume were studied by means of salt spray test and outdoor exposure test. Edge creep progress behavior in salt spray test was different from that in outdoor exposure test. According to the results of outdoor exposure test for up to 10 years, the edge creep of prepainted Galvalume is more appreciable than that of the prepainted galvanized steel sheet in the early stages of exposure. However, the edge creep rate of prepainted Galvalume decreases with the lapse of time while that of prepainted galvanized steel sheet is kept almost constant. As the results, edge creep width becomes larger in galvanized steel sheet than in Galvalume in 7 to 9 years of exposure. Meanwhile in salt spray test, edge creep width of prepainted galvanized steel sheet does not exceed that of prepainted Galvalume up to 1 000 h of exposure. Effects of pretreatments and coatings were not clearly noticed except that special primer for Galvalume decreased edge creep width of prepainted Galvalume in salt spray test.
引用
收藏
页码：1130 / 1137
页数：8
相关论文
共 50 条
  • [21] Influence of organic composite coating components on various properties of 55%Al-Zn alloy coated steel sheet
    Matsuzaki, A
    Yamaji, T
    Yoshida, K
    Yamashita, M
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2003, 89 (01): : 123 - 127
  • [22] OXIDATION RESISTANCE OF ZN-AL ALLOY COATED STEEL SHEET
    NUMAKURA, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 : 1227 - 1227
  • [23] RESISTANCE OF AL, ZN, AND 55-PERCENT AL-ZN-COATED STEELS TO ATMOSPHERIC CORROSION INVOLVING STAGNANT WATER
    ALLEGRA, L
    TOWNSEND, HE
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1980, 127 (08) : C362 - C362
  • [24] Cut-edge corrosion of a Zn-55Al-coated steel: A comparison between sulphate and chloride solutions
    Vu, A. Q.
    Vuillemin, B.
    Oltra, R.
    Allely, C.
    CORROSION SCIENCE, 2011, 53 (09) : 3016 - 3025
  • [25] ATMOSPHERIC GALVANIC PROTECTION OF 55-PERCENT AL-ZN PRECOATED STEEL
    MORCILLO, M
    PALMA, E
    FERNANDEZ, B
    WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1994, 45 (10): : 550 - 553
  • [26] FORMABILITY OF ZN-55AL ALLOY COATED LAYER ON STEEL SHEETS
    YAMADA, M
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (05): : S453 - S453
  • [27] Polypyrrole film on 55% Al-Zn-coated steel for corrosion prevention
    Ryu, Haku
    Sheng, Nan
    Ohtsuka, Toshiaki
    Fujita, Sakae
    Kajiyama, Hiroshi
    CORROSION SCIENCE, 2012, 56 : 67 - 77
  • [28] Edge creep control ability of rust prevention paints and anticorrosive pigments for 55% Al-Zn-plated steel sheets
    Matsuda H.
    Ooshima T.
    Hayami Y.
    Zairyo to Kankyo/ Corrosion Engineering, 2010, 59 (09): : 341 - 348
  • [29] Development of a new organic composite coating for enhancing corrosion resistance of 55% Al-Zn alloy coated steel sheet
    Matsuzaki, A
    Yamaji, T
    Yamashita, M
    SURFACE & COATINGS TECHNOLOGY, 2003, 169 : 655 - 657
  • [30] Electrochemical behavior of a chromated 55mass%Al-Zn coated steel sheet before and after a heat treatment
    Nogueira, TMC
    Cruz, MAS
    Rios, PR
    ISIJ INTERNATIONAL, 2000, 40 (08) : 824 - 826
12345