THE EFFECT OF WET UNDERWATER WELDING ON COLD CRACKING SUSCEPTIBILITY OF DUPLEX STAINLESS STEEL

被引：31
|
作者：
Labanowski, J. [1 ]
Prokop-Strzelczynska, K. [1 ]
Rogalski, G. [1 ]
Fydrych, D. [1 ]
机构：
[1] Gdansk Univ Technol, Dept Mat & Welding Engn, Fac Mech Engn, 11-12 Narutowicza St, PL-80233 Gdansk, Poland
来源：
ADVANCES IN MATERIALS SCIENCE | 2016年 / 16卷 / 02期
关键词：
duplex stainless steel; underwater welding; cold cracking;
D O I：
10.1515/adms-2016-0010
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The present work was conducted to assess the weldability of duplex stainless steel in underwater conditions. Metal manual arc welding (MMA) with the use of coated electrodes was used in the investigations. Tekken weldability tests were performed underwater at 0.5 m depth and in the air. Nondestructive tests, metallographic examinations of welds, ferrite content assessment in microstructure and hardness test were performed. The good weldability at underwater conditions of duplex stainless with the use of MMA method was confirmed, however difficulties in stable arc burning were revealed.
引用
收藏
页码：68 / 77
页数：10
相关论文
共 50 条
  • [31] Cracking of duplex stainless steel due to dissolved hydrogen
    Natl Tsing Hua Univ, Hsinchu, Taiwan
    Metall Mat Trans A Phys Metall Mat Sci, 5 (1079-1085):
  • [32] Characterization of weld solidification cracking in a duplex stainless steel
    Varol, I., 1600, (23):
  • [33] DELAYED CRACKING IN DUPLEX STAINLESS-STEEL STUDIED
    不详
    MATERIALS PERFORMANCE, 1995, 34 (07) : 56 - 56
  • [34] Effect of solidification behaviour of austenitic stainless steel on the solidification cracking susceptibility
    Liu, R. (lrp_msc@nuaa.edu.cn), 2005, China Welding (14):
  • [35] Investigation of arc stability, microstructure evolution and corrosion resistance in underwater wet FCAW of duplex stainless steel
    Ma, Qiang
    Luo, Chuncheng
    Liu, Shixiong
    Li, Hongliang
    Wang, Pengfei
    Liu, Duo
    Lei, Yucheng
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2021, 15 : 5482 - 5495
  • [36] The effect of solidification behaviour of austenitic stainless steel on the solidification cracking susceptibility
    刘仁培
    董祖珏
    潘永明
    China Welding, 2005, (01) : 38 - 43
  • [37] Evaluation of the sigma phase precipitation susceptibility in duplex stainless steel SAF2205 welding
    Fonseca, Camila Soares
    da Silva, Sidney Nicodemos
    Gomes, Henrique Giacomini
    Silva, Danillo Wisky
    Guimaraes Junior, Jose Benedito
    Pinheiro, Ivete Peixoto
    MATERIA-RIO DE JANEIRO, 2019, 24 (03):
  • [38] Effect of Hydrogen on Cold Cracking of Welds in Pipe Steel Welding.
    Mandel'berg, S.L.
    Buslinskii, S.V.
    Bogachek, Yu.L.
    Avtomaticheskaya Svarka, 1985, (02):
  • [39] Effect of nitrogen content on the environmentally-assisted cracking susceptibility of duplex stainless steels
    Chuan-Ming Tseng
    Wen-Ta Tsai
    Horng-Yih Liou
    Metallurgical and Materials Transactions A, 2003, 34 : 95 - 103
  • [40] Effect of nitrogen content on the environmentally-assisted cracking susceptibility of duplex stainless steels
    Tseng, CM
    Liou, HY
    Tsai, WT
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2003, 34 (01): : 95 - 103
12345