A MODEL TO PREDICT THE FAILURE OF ZIRCALOY-4 FUEL SHEATHING DURING POSTULATED LOCA CONDITIONS

被引：31
|
作者：
ROSINGER, HE
机构：
来源：
JOURNAL OF NUCLEAR MATERIALS | 1984年 / 120卷 / 01期
关键词：
D O I：
10.1016/0022-3115(84)90169-7
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
引用
收藏
页码：41 / 54
页数：14
相关论文
共 50 条
  • [41] Burst criterion for zircaloy-4 fuel cladding in an inert environment
    Khan, Mohd. Kaleem
    Pathak, Manabendra
    Deo, Anuj K.
    Singh, Ritu
    NUCLEAR ENGINEERING AND DESIGN, 2013, 265 : 886 - 894
  • [42] Reflection on the ductility of irradiated zircaloy-4 fuel rod cladding
    Sauer, G.
    KERNTECHNIK, 2010, 75 (06) : 337 - 341
  • [43] Embrittlement of pre-hydrided Zircaloy-4 by steam oxidation under simulated LOCA transients
    Desquines, J.
    Drouan, D.
    Guilbert, S.
    Lacote, P.
    JOURNAL OF NUCLEAR MATERIALS, 2016, 469 : 20 - 31
  • [44] Fracture mechanics analysis of Zircaloy-4 tubular samples after laboratory simulated LOCA transient
    Desquines, J.
    Guilbert, S.
    Taurines, T.
    Busser, V.
    ENGINEERING FRACTURE MECHANICS, 2018, 193 : 96 - 107
  • [45] A model to describe the mechanical behavior and the ductile failure of hydrided Zircaloy-4 fuel claddings between 25 °C and 480 °C
    Le Saux, M.
    Besson, J.
    Carassou, S.
    JOURNAL OF NUCLEAR MATERIALS, 2015, 466 : 43 - 55
  • [46] An attempt for a unified description of mechanical testing on Zircaloy-4 cladding subjected to simulated LOCA transient
    Desquines, Jean
    Drouan, Doris
    Torres, Elodie
    Guilbert, Severine
    Lacote, Pauline
    EPJ NUCLEAR SCIENCES & TECHNOLOGIES, 2016, 2
  • [47] HYDRIDE BEHAVIOR IN ZIRCALOY-4 DURING THERMOMECHANICAL CYCLING
    Colas, Kimberly
    Motta, Arthur
    Daymond, Mark R.
    Almer, Jonathan
    Cai, Zhonghou
    15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, : 683 - 688
  • [48] A model to describe the anisotropic viscoplastic mechanical behavior of fresh and irradiated Zircaloy-4 fuel claddings under RIA loading conditions
    Le Saux, M.
    Besson, J.
    Carassou, S.
    Poussard, C.
    Averty, X.
    JOURNAL OF NUCLEAR MATERIALS, 2008, 378 (01) : 60 - 69
  • [49] EDDY-CURRENT EXAMINATION TECHNIQUE DURING MANUFACTURING OF ZIRCALOY-4 FUEL CLADDING TUBES
    SENEVAT, J
    MAINY, P
    JOURNAL OF NUCLEAR MATERIALS, 1991, 178 (2-3) : 315 - 320
  • [50] THE EFFECT OF VARYING SAMPLE GEOMETRY ON THE FAILURE PROPERTIES OF ZIRCALOY-4
    RAWERS, JC
    SIZEMORE, J
    ENGINEERING FRACTURE MECHANICS, 1987, 27 (02) : 205 - 214
12345