EVALUATION OF STEEL 20Kh13 NOZZLE FOR STRESS CORROSION UNDER PETROLEUM PROCESSING CONDITIONS

被引：0
|
作者：
Davydkin, M. V. [1 ]
Zolotenin, G. G. [1 ]
Gabaidulin, D. Yu. [1 ]
Nemykina, O. V. [2 ]
机构：
[1] Irkutsk Res & Design Inst Chem & Petrochem Engn, Irkutsk, Russia
[2] Irkutsk State Tech Univ, Irkutsk, Russia
来源：
CHEMICAL AND PETROLEUM ENGINEERING | 2015年 / 50卷 / 11-12期
关键词：
corrosion cracking; high pressure; nozzles; test results;
D O I：
10.1007/s10556-015-9971-9
中图分类号：
TQ [化学工业];
学科分类号：
0817 ;
摘要：
Specimens and standard shut-off valve components made of steel 20Kh13 are tested for resistance to hydrogen sulfide corrosion cracking at high pressure and temperature, and test results are provided.
引用
收藏
页码：739 / 744
页数：6
相关论文
共 50 条
  • [31] CORROSION RESISTANCE OF WELDED JOINTS IN STEEL 07Kh13AG20.
    Glazkova, S.A.
    Karasyuk, T.N.
    Bukanova, G.S.
    Zheltova, G.A.
    Leibzon, V.M.
    Kalinin, B.P.
    Chemical and Petroleum Engineering, 1985, 21 (02) : 90 - 92
  • [32] CORROSION OF 14KH17N2 STEEL UNDER INDUSTRIAL CONDITIONS
    ALIMOV, VI
    ONOPRIENKO, VG
    SHIRYAEV, VT
    PROTECTION OF METALS, 1986, 22 (04): : 458 - 459
  • [33] Corrosion Cracking of Kh70 Pipe Steel under the Conditions of Cathodic Protection
    Nyrkova, L., I
    MATERIALS SCIENCE, 2020, 56 (02) : 273 - 278
  • [34] Corrosion Cracking of Kh70 Pipe Steel under the Conditions of Cathodic Protection
    L. I. Nyrkova
    Materials Science, 2020, 56 : 273 - 278
  • [35] CORROSION OF 14Kh17N2 STEEL UNDER INDUSTRIAL CONDITIONS.
    Alimov, V.I.
    Onoprienko, V.G.
    Shiryaev, V.T.
    Protection of Metals (English translation of Zaschita Metallov), 1986, 22 (04): : 458 - 459
  • [36] An evaluation of carbon steel corrosion under stagnant seawater conditions
    Lee, JS
    Ray, RI
    Lemieux, EJ
    Falster, AU
    Little, BJ
    BIOFOULING, 2004, 20 (4-5) : 237 - 247
  • [37] ENHANCING THE STRESS-CORROSION CRACKING RESISTANCE OF HIGH-STRENGTH STEEL KH13
    ZHIGACHEVA, NI
    NAZAROV, AA
    PROTECTION OF METALS, 1983, 19 (04): : 446 - 451
  • [38] RESISTANCE OF STEEL 07KH13AG20 TO PITTING CORROSION DURING COOKING OF RAW STARCH
    YAVOR, VA
    DVORNICHENKO, MV
    PROTECTION OF METALS, 1985, 21 (06): : 768 - 769
  • [39] The Effect of Microstructure on the Corrosion Resistance of Pipe Steel 20 under Conditions of Carbon Dioxide Corrosion
    Laurinavichyute, V. K.
    Shibaeva, T., V
    Pugolovkin, L., V
    Zheleznyi, M., V
    Pyshmintsev, I. Yu
    Mal'tseva, A. N.
    Chepik, F. D.
    RUSSIAN JOURNAL OF ELECTROCHEMISTRY, 2022, 58 (03) : 226 - 234
  • [40] The Effect of Microstructure on the Corrosion Resistance of Pipe Steel 20 under Conditions of Carbon Dioxide Corrosion
    V. K. Laurinavichyute
    T. V. Shibaeva
    L. V. Pugolovkin
    M. V. Zheleznyi
    I. Yu. Pyshmintsev
    A. N. Mal’tseva
    F. D. Chepik
    Russian Journal of Electrochemistry, 2022, 58 : 226 - 234
12345