THE PASSIVITY OF IRON AND CARBON-STEEL IN ANHYDROUS PROPYLENE CARBONATE SOLUTIONS

被引：18
|
作者：
SHIFLER, DA [1 ]
MORAN, PJ [1 ]
KRUGER, J [1 ]
机构：
[1] USN ACAD,DEPT MECH ENGN,ANNAPOLIS,MD 21402
来源：
CORROSION SCIENCE | 1991年 / 32卷 / 5-6期
关键词：
D O I：
10.1016/0010-938X(91)90102-U
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The passivation behavior of high purity iron and 1018 carbon steel in anhydrous propylene carbonate (PC) containing 0.5 M LiClO4 or 0.5 M LiAsF6 was studied. The air-formed film on Fe was stable and protective over a wide applied potential range in perchlorate solutions. Scratch tests showed that both bare Fe and steel passivate in the anhydrous PC solutions of either electrolyte by chemisorption of PC molecules below the oxidation potential of PC (PC(ox). At higher potentials, bare Fe passivates in PC/LiClO4 via the formation of a Fe(ClO4)2 salt film. The air-formed film on carbon steel was protective up to the PC(ox) potential in either electrolyte. Above PC(ox), deterioration of the air-formed film on steel was associated with sulfide surface inclusions. Pits initiated and grew at these inclusion sites. Scratch tests showed slower repassivation of the bare steel by the Fe(ClO4)2 salt film than on iron. Sulfides impeded this repassivation. Above PC(ox), neither the iron or the steel are in passive in PC/LiAsF6 solutions. The higher solubility of the Fe(AsF6)2 salt prevents precipitation of a protective salt film.
引用
收藏
页码：475 / 496
页数：22
相关论文
共 50 条
  • [21] The effects of sulfides on the passivity of carbon steel in organic solutions
    Shifler, DA
    Moran, PJ
    Kruger, J
    ELECTROCHIMICA ACTA, 1997, 42 (04) : 567 - 577
  • [22] Influence of passivity on the tribocorrosion of carbon steel in aqueous solutions
    Mischler, S.
    Spiegel, A.
    Stemp, M.
    Landolt, D.
    Wear, 2001, 250-251 (PART 2) : 1295 - 1307
  • [23] EXTRACTION OF IRON(III) FROM PERCHLORATE SOLUTIONS INTO PROPYLENE CARBONATE
    ITOH, H
    MURATA, K
    IKEDA, S
    JOURNAL OF INORGANIC & NUCLEAR CHEMISTRY, 1973, 35 (10): : 3632 - 3636
  • [24] IRON NITRIDE AND CARBONITRIDE PHASES IN A NITROGEN IMPLANTED CARBON-STEEL
    DOSSANTOS, CA
    DEBARROS, BAS
    DESOUZA, JP
    BAUMVOL, IJR
    APPLIED PHYSICS LETTERS, 1982, 41 (03) : 237 - 239
  • [25] CORROSION STUDIES OF ION-IMPLANTED IRON AND CARBON-STEEL
    BRAUN, M
    HULTBERG, S
    BROWN, A
    SVENSSON, BM
    HOGMARK, S
    NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1987, 19-20 : 259 - 262
  • [26] DISSOLUTION OF IRON DURING THE INITIAL CORROSION OF CARBON-STEEL IN AQUEOUS H2S SOLUTIONS
    TEWARI, PH
    CAMPBELL, AB
    CANADIAN JOURNAL OF CHEMISTRY, 1979, 57 (02) : 188 - 196
  • [27] CERTIFICATION OF STANDARD SAMPLES OF CAST-IRON AND CARBON-STEEL
    FEDOROVA, SF
    NUSTROVA, VS
    FOKINA, LS
    SHORINA, ZG
    BUGUMANOVA, LG
    KOSTROMINA, TP
    SHALAMOVA, VS
    SHCHUKINA, MY
    INDUSTRIAL LABORATORY, 1991, 57 (07): : 678 - 680
  • [28] THE PITTING OF IRON AND CARBON-STEEL IN MIXTURES OF METHANOL-WATER
    PISCHIK, LM
    NOVITSKII, VS
    LYSAK, TA
    PROTECTION OF METALS, 1986, 22 (03): : 333 - 335
  • [29] THE INFLUENCE OF THE STATE OF THE SURFACE ON THE ELECTROCHEMISTRY OF IRON AND CARBON-STEEL ELECTRODES IN AQUEOUS CO2 SOLUTIONS
    VIDEM, K
    SURFACE SCIENCE, 1995, 335 (1-3) : 235 - 240
  • [30] DIFFUSION BONDING OF GREY CAST-IRON TO ARMCO IRON AND A CARBON-STEEL
    CALVO, FA
    URENA, A
    DESALAZAR, JMG
    MOLLEDA, F
    JOURNAL OF MATERIALS SCIENCE, 1989, 24 (11) : 4152 - 4159
12345