Comparative study on the corrosion behavior of the cold rolled and hot rolled low-alloy steels containing copper and antimony in flue gas desulfurization environment

被引：1
|
作者：
S. A. Park
J. G. Kim
Y. S. He
K. S. Shin
J. B. Yoon
机构：
[1] Sungkyunkwan University,Department of Advanced Materials Engineering
[2] Changwon National University,School of Nano Materials Engineering
[3] POSCO Technical Research Lab.,undefined
来源：
The Physics of Metals and Metallography | 2014年 / 115卷
关键词：
cold rolled steel; hot rolled steel; corrosion; inclusion; grain refinement; grain orientation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The correlation between the corrosion and microstructual characteristics of cold rolled and hot rolled low-alloy steels containing copper and antimony was established. The corrosion behavior of the specimens used in flue gas desulfurization systems was examined by electrochemical and weight loss measurements in an aggressive solution of 16.9 vol % H2SO4 + 0.35 vol % HCl at 60°C, pH 0.3. It has been shown that the corrosion rate of hot rolled steel is lower than that of cold rolled steel. The corrosion rate of cold rolled steel was increased by grain refinement, inclusion formation, and preferred grain orientation.
引用
收藏
页码：1285 / 1294
页数：9
相关论文
共 50 条
  • [31] Creation of an Effective Technology for the Production of Cold-Rolled High-Strength Low-Alloy Steels with High and Stable Properties. Part 1. Hot-rolled Products
    A. I. Zaytsev
    A. I. Dagman
    A. B. Stepanov
    A. V. Koldaev
    D. A. Kovalev
    Metallurgist, 2022, 66 : 243 - 254
  • [32] Carbide precipitation and high-temperature strength of hot-rolled high-strength, low-alloy steels containing Nb and Mo
    Lee, WB
    Hong, SG
    Park, CG
    Park, SH
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2002, 33 (06): : 1689 - 1698
  • [33] Carbide precipitation and high-temperature strength of hot-rolled high-strength, low-alloy steels containing Nb and Mo
    Won-Beom Lee
    Seung-Gab Hong
    Chan-Gyung Park
    Sung-Ho Park
    Metallurgical and Materials Transactions A, 2002, 33 : 1689 - 1698
  • [34] STRUCTURE AND PROPERTIES OF HEAVILY COLD-ROLLED IRON AND HIGH-STRENGTH LOW-ALLOY AND LOW-CARBON STEELS
    ROVEN, HJ
    NES, E
    METAL SCIENCE, 1984, 18 (11): : 515 - 520
  • [35] SECM Study of Effect of Chromium Content on the Localized Corrosion Behavior of Low-Alloy Steels in Chloride Environment
    Indira, K.
    Nishimura, T.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2016, 25 (10) : 4157 - 4170
  • [36] SECM Study of Effect of Chromium Content on the Localized Corrosion Behavior of Low-Alloy Steels in Chloride Environment
    K. Indira
    T. Nishimura
    Journal of Materials Engineering and Performance, 2016, 25 : 4157 - 4170
  • [37] CORROSION KINETICS OF LOW-ALLOY AND HIGH-ALLOY STEELS IN CHLORINE-CONTAINING GAS ATMOSPHERES
    HAANAPPEL, VAC
    HAANAPPEL, NWJ
    FRANSEN, T
    VANCORBACH, HD
    GELLINGS, PJ
    CORROSION, 1992, 48 (10) : 812 - 821
  • [38] Creation of an Effective Technology for the Production of Cold-Rolled High-Strength Low-Alloy Steels with High and Stable Properties. Part 2. Cold-rolled Products
    Zaitsev, A., I
    Dagman, A., I
    Stepanov, A. B.
    Koldaev, A., V
    Rodionova, I. G.
    Orekhov, M. E.
    METALLURGIST, 2022, 66 (3-4) : 359 - 367
  • [39] INCREASING OF THE LEVEL AND STABILITY OF HOT- AND COLD-ROLLED METAL CHARACTERISTICS USING PURPOSEFUL NANOSTRUCTURING OF HIGH-STRENGTH LOW-ALLOY ELECTRIC STEELS
    Shakhpazov, Evgenij Khristoforovich
    Zaytsev, Aleksandr Ivanovich
    Rodionova, Irina Gavrilovna
    NANOTECHNOLOGIES IN CONSTRUCTION-A SCIENTIFIC INTERNET-JOURNAL, 2010, 2 (06): : 68 - 86
  • [40] Metallurgical Effects of a Novel Tundish Refining Process for High-Strength Low-Alloy Hot-Rolled Plate Steels
    Isayev, O.
    Kislitsa, V.
    Zhang, C.
    Wu, K.
    Hress, A.
    METALLURGIST, 2016, 59 (9-10) : 980 - 986
12345