Influence of laser conditioning on laser induced damage threshold of single layers of ZrO2 with various deposition conditions

被引：0
|
作者：
M. Sahraee
H. Reza Fallah
H. Zabolian
B. Moradi
M. Haji Mahmoodzade
机构：
[1] University of Isfahan,Physics Department
[2] University of Isfahan,Isfahan Quantum Optics Group
来源：
Optics and Spectroscopy | 2015年 / 118卷
关键词：
Single Layer; Oxygen Partial Pressure; Electron Beam Evaporation; Spectral Transmittance; Laser Damage;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Single layers of ZrO2 were coated at base pressure of 10−5 mbar by electron beam evaporation (EBE) technique. The influence of oxygen partial pressure on spectral properties and laser induced damage threshold (LIDT) of the samples were investigated. Spectral transmittance of the samples was measured by spectrophotometer. Laser induced damage threshold was detected according to ISO standard 11254. Laser conditioning was conducted by scanning the surface of the samples. Results showed that laser damage resistance was enhanced by increasing the oxygen partial pressure during deposition. LIDT of the samples was changed after laser conditioning. Experimental results revealed that there is enhancement of laser damage resistance of the samples with higher oxygen partial pressure after laser conditioning.
引用
收藏
页码：627 / 630
页数：3
相关论文
共 50 条
  • [1] Influence of Laser Conditioning on Laser Induced Damage Threshold of Single Layers of ZrO2 with Various Deposition Conditions
    Sahraee, M.
    Fallah, H. Reza
    Zabolian, H.
    Moradi, B.
    Mahmoodzade, M. Haji
    OPTICS AND SPECTROSCOPY, 2015, 118 (04) : 627 - 630
  • [2] The effect of porosity on the laser induced damage threshold of TiO2 and ZrO2 single layer films
    Bananej, Alireza
    Hassanpour, Arnir
    Razzaghi, Hossein
    Zade, Mehdi Vaez
    Mohammadi, Ali
    OPTICS AND LASER TECHNOLOGY, 2010, 42 (08): : 1187 - 1192
  • [3] Effect of annealing on microstructure and laser-induced damage threshold of ZrO2 Coatings
    Tian, Guang-Lei
    Huang, Jian-Bing
    He, Hong-Bo
    Shao, Jian-Da
    Qiangjiguang Yu Lizishu/High Power Laser and Particle Beams, 2005, 17 (02): : 217 - 221
  • [4] Microstructure and laser-induced damage threshold of ZrO2 coatings dependence on annealing temperature
    Tian, GL
    Huang, JB
    Wang, T
    He, HB
    Shao, JD
    APPLIED SURFACE SCIENCE, 2005, 239 (02) : 201 - 208
  • [5] Laser-conditioning mechanism of ZrO2/SiO2 HR films with fitting damage probability curves of laser-induced damage
    李笑
    刘晓凤
    赵元安
    邵建达
    范正修
    ChineseOpticsLetters, 2010, 8 (06) : 598 - 600
  • [6] Laser-conditioning mechanism of ZrO2/SiO2 HR films with fitting damage probability curves of laser-induced damage
    Li, Xiao
    Liu, Xiaofeng
    Zhao, Yuan'an
    Shao, Jianda
    Fan, Zhengxiu
    CHINESE OPTICS LETTERS, 2010, 8 (06) : 598 - 600
  • [7] Influence of glass surface layers on laser-induced damage threshold
    Gu, ZT
    Liang, PH
    Zhang, WQ
    LASER-INDUCED DAMAGE IN OPTICAL MATERIALS: 2001 PROCEEDINGS, 2002, 4679 : 75 - 78
  • [8] Influence of porosity on laser damage threshold of sol-gel ZrO2 and SiO2 monolayer films
    Guo, Y. J.
    Zu, X. T.
    Yuan, X. D.
    Jiang, X. D.
    OPTIK, 2012, 123 (06): : 479 - 484
  • [9] Excimer laser fabrication of polycrystalline ZrO2 layers
    Starbov, N
    Mednikarov, B
    Mankov, V
    Georgiev, DG
    Hanus, F
    Kolev, K
    Laude, LD
    THIN FILMS - STRUCTURE AND MORPHOLOGY, 1997, 441 : 217 - 222
  • [10] Effects of ultrasonics cleaning and laser conditioning on the laser induced damage threshold of the antireflection
    Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, P.O. Box 800-211, Shanghai 201800, China
    Qiangjiguang Yu Lizishu, 2006, 10 (1712-1716):
12345