Phase Equilibria in the Ternary Al–Ti–Pt System. III. The Al–Ti–Pt Melting Diagram in the Composition Range 0–50 at.% Pt

被引：0
|
作者：
O. V. Zaikina
V. G. Khoruzhaya
K. Ye. Korniyenko
T. Ya. Velikanova
机构：
[1] National Academy of Sciences of Ukraine,Frantsevich Institute for Problems of Materials Science
来源：
Powder Metallurgy and Metal Ceramics | 2019年 / 58卷
关键词：
phase equilibria; melting diagram; Scheil diagram; ternary compound; invariant equilibrium;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The melting diagram and reaction scheme (Scheil diagram) of the Al–Ti–Pt system have been constructed for the first time in the composition range 0–50 at.% Pt using the experimental results for as-cast alloys and alloys annealed at subsolidus temperatures. It is established that ternary compounds τ3, τ4, and τ8 form congruently with participation of the liquid phase and compounds τ1, τ2, τ5, τ6, τ7, τ9, and τ11 by peritectic reactions. All compounds take part in phase equilibria with participation of the liquid phase, forming 31 four-phase and 28 three-phase invariant equilibria at temperatures from 1410 to 660°C.
引用
收藏
页码：81 / 88
页数：7
相关论文
共 50 条
  • [21] CONSTITUTION OF ALLOYS AND PHASE DIAGRAM OF THE Al-Ti-Rh SYSTEM. III. SOLIDUS SURFACE OF THE Ti-TiRh-AlRh-Al PARTIAL SYSTEM
    Kornienko, K. E.
    Khoruzha, V. G.
    Vereshchaka, V. M.
    POWDER METALLURGY AND METAL CERAMICS, 2012, 50 (9-10) : 641 - 654
  • [22] Laves phases in the ternary systems Ti-{Pd, Pt}-Al
    Yan, Xinlin
    Grytsiv, A.
    Rogl, P.
    Schmidt, H.
    Giester, G.
    Saccone, A.
    Chen, Xing-Qiu
    INTERMETALLICS, 2009, 17 (05) : 336 - 342
  • [23] Constitution of alloys and phase diagram of the Al-Ti-Rh system. IV. Melting diagram of the Ti-TiRh-AlRh-Al partial system
    Kornienko, K. E.
    Khoruzha, V. G.
    POWDER METALLURGY AND METAL CERAMICS, 2012, 50 (11-12) : 726 - 739
  • [24] Experimental Study on Phase Equilibria in Ti-Cu-Pt System
    Y. Zhong
    H. S. Liu
    G. M. Cai
    Z. P. Jin
    Journal of Phase Equilibria and Diffusion, 2017, 38 : 466 - 476
  • [25] Experimental Study on Phase Equilibria in Ti-Cu-Pt System
    Zhong, Y.
    Liu, H. S.
    Cai, G. M.
    Jin, Z. P.
    JOURNAL OF PHASE EQUILIBRIA AND DIFFUSION, 2017, 38 (04) : 466 - 476
  • [26] Gd-Al and Dy-Al Systems: Phase Equilibria in the 0 to 66.7 at.% Al Composition Range
    Saccone, Adriana
    Cardinale, Anna Maria
    Delfino, Stefano
    Ferro, Riccardo
    International Journal of Materials Research, 2000, 91 (01) : 17 - 23
  • [27] A STUDY OF THE Al-Ni-Pt ALLOY SYSTEM. PHASE EQUILIBRIA AT 1100 AND 1300 °C
    Grushko, B.
    Kapush, D.
    Konoval, V.
    Shemet, V.
    POWDER METALLURGY AND METAL CERAMICS, 2011, 50 (7-8) : 462 - 470
  • [28] A study of the Al-Ni-Pt alloy system. Phase equilibria at 1100 and 1300°C
    B. Grushko
    D. Kapush
    V. Konoval
    V. Shemet
    Powder Metallurgy and Metal Ceramics, 2011, 50 : 462 - 470
  • [29] Gd-Al and Dy-Al systems: Phase equilibria in the 0 to 66.7 at. % Al composition range
    Saccone, A
    Cardinale, AM
    Delfino, S
    Ferro, R
    ZEITSCHRIFT FUR METALLKUNDE, 2000, 91 (01): : 17 - 23
  • [30] High temperature phase equilibria near Ti-50 at% Al composition in Ti-Al system studied by directional solidification
    Jung, IS
    Kim, MC
    Lee, JH
    Oh, MH
    Wee, DM
    INTERMETALLICS, 1999, 7 (11) : 1247 - 1253
12345