Magnetoresistive properties of cold-pressed CrO2 powder, prepared by hydrothermal synthesis

The resistive, magnetoresistive and magnetic properties of cold-pressed CrO2, powder prepared by hydrothermal synthesis from chromic anhydride have been studied. The powder particles (with a mean diameter of about 120 nm) were nearly spherical. The particles stabilized with a β-CrOOH surface layer. The powder compact (with a Curie temperature of about 385 K) revealed nonmetallic temperature behavior of the resistance (with an R(T) dependence close to exponential at T < 20 K). A giant negative magnetoresistance (MR) (∼20% at T ≈ 5K) is found. MR decreased rapidly with an increase in temperature (to 0.3% at T > 200 K). Such MR behavior is shown to be typical of a system of magnetic grains with magnetic (spin-dependent) tunneling.