Accelerated corrosion tests for electroplated metals

被引：0
|
作者：
V. V. Khmelyov
S. N. Kozhevnikova
Yu. N. Novosyolov
机构：
[1] Iskra Scientific and Production Association (NPO Iskra),
来源：
Chemical and Petroleum Engineering | 2012年 / 47卷 / 11-12期
关键词：
Corrosion Rate; Zinc Coating; Atmospheric Corrosion; Marine Atmosphere; Accelerate Corrosion Test;
D O I：
10.1007/s10556-012-9562-y
中图分类号：
学科分类号：
摘要：
A procedure and results are provided for accelerated corrosion testing of zinc, cadmium, and copper coatings for gas-pumping unit and gas turbine power station metal components. The best retention, climatic and corrosion resistance is demonstrated by zinc coating. According to test results, electroplated coatings are recommended for protection over a prolonged (up to 25 years) operating life.
引用
收藏
页码：854 / 857
页数：3
相关论文
共 50 条
  • [31] SELECTING ELECTROPLATED METALS
    MISSEL, L
    METAL PROGRESS, 1970, 97 (06): : 110 - &
  • [32] Accelerated corrosion tests for corrosion protection systems on steel sheet for the automotive industry
    Androsch, FM
    Kösters, K
    Stellnberger, KH
    STAHL UND EISEN, 2001, 121 (06): : 37 - 46
  • [33] Accelerated corrosion tests in the automotive industry: A comparison of the performance towards cosmetic corrosion
    LeBozec, N.
    Blandin, N.
    Thierry, D.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2008, 59 (11): : 889 - 894
  • [34] Corrosion of exposed rebars, associated mechanical degradation and correlation with accelerated corrosion tests
    Papadopoulos, M. P.
    Apostolopoulos, C. A.
    Zervaki, A. D.
    Haidemenopoulos, G. N.
    CONSTRUCTION AND BUILDING MATERIALS, 2011, 25 (08) : 3367 - 3374
  • [35] DCTC®:: Dry corrosion test cabinet: A new tool for accelerated corrosion tests
    Rossini, I
    INSTITUTE OF ENVIRONMENTAL SCIENCES AND TECHNOLOGY - 1998 PROCEEDINGS: DESIGN, TEST, AND EVALUATION PRODUCT RELIABILITY, 1998, : 259 - 263
  • [36] Outdoor exposure tests of electroplated nickel and chromium coatings on steel and nonferrous metals.
    Blum, W
    Strausser, PWC
    JOURNAL OF RESEARCH OF THE NATIONAL BUREAU OF STANDARDS, 1940, 24 (04): : 443 - 474
  • [37] Wear-accelerated corrosion of passive metals in tribocorrosion systems
    Ecole Polytechnique Federale de, Lausanne, Lausanne, Switzerland
    J Electrochem Soc, 3 (750-758):
  • [38] Wear-accelerated corrosion of passive metals in tribocorrosion systems
    Mischler, S
    Debaud, S
    Landolt, D
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1998, 145 (03) : 750 - 758
  • [39] ACCELERATED CORROSION CRACKING TESTS OF HARDENED SHEET MATERIALS.
    Rekhter, D.Z.
    Freid, M.Kh.
    Suprunov, V.A.
    Industrial Laboratory (USSR) (English translation of Zavodskaya Laboratoriya), 1975, 41 (05): : 746 - 748
  • [40] ACCELERATED CORROSION CRACKING TESTS OF STEELS IN ACTIVE PASSIVE LOADING
    MUIZHNEK, IA
    SOVIET MATERIALS SCIENCE, 1990, 26 (02): : 168 - 171
12345