Dependence of the period of subcritical growth of a creep fatigue crack on the duration of loading cycles

被引：0
|
作者：
O. E. Andreikiv
R. M. Lesiv
I. Ya. Dolins’ka
机构：
[1] Franko Lviv National University,
来源：
Materials Science | 2009年 / 45卷
关键词：
creep fatigue crack; subcritical crack growth; residual service life; energy-balance equation; high-temperature creep; duration of loading cycle;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
We construct the kinetic equation for the period of growth of a creep fatigue crack. By using the experimental data, it is shown that this equation correctly describes the behavior of the crack. It follows from the solution of Sack’s problem that the larger the duration of the loading cycle T, the more pronounced the effect of creep and, hence, the smaller the residual service life of the structure.
引用
收藏
页码：494 / 503
页数：9
相关论文
共 50 条
  • [31] Fatigue and creep crack growth in asphalt materials
    Zuidema, J
    Pronk, A
    Tolman, F
    PROGRESS IN MECHANICAL BEHAVIOUR OF MATERIALS (ICM8), VOL 1: FATIGUE AND FRACTURE, 1999, : 424 - 428
  • [32] CRACK GROWTH UNDER CREEP AND FATIGUE CONDITIONS
    SADANANDA, K
    SHAHINIAN, P
    JOURNAL OF METALS, 1979, 31 (08): : F37 - F38
  • [33] Fatigue crack growth under ultrasonic fatigue loading
    Ni, JG
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1997, 20 (01) : 23 - 28
  • [34] Determination of the Period of Subcritical Growth of Creep Cracks in Steam Pipelines
    O. E. Andreikiv
    N. B. Sas
    Materials Science, 2014, 49 : 624 - 630
  • [35] Estimation of the Subcritical Growth Period for a Through Crack of High-Temperature Creep in a Two-Layer Plate
    O. E. Andreikiv
    V. R. Skal’s’kyi
    I. Ya. Dolins’ka
    L. N. Dobrovol’s’ka
    Strength of Materials, 2014, 46 : 328 - 335
  • [36] Estimation of the Subcritical Growth Period for a Through Crack of High-Temperature Creep in a Two-Layer Plate
    Andreikiv, O. E.
    Skal's'kyi, V. R.
    Dolins'ka, I. Ya.
    Dobrovol's'ka, L. N.
    STRENGTH OF MATERIALS, 2014, 46 (03) : 328 - 335
  • [37] Determination of the Period of Subcritical Growth of Creep Cracks in Steam Pipelines
    Andreikiv, O. E.
    Sas, N. B.
    MATERIALS SCIENCE, 2014, 49 (05) : 624 - 630
  • [38] High temperature crack growth behavior of 304 stainless steel under creep and fatigue loading
    Baik, YM
    Kim, KS
    ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4, 2005, 297-300 : 452 - 457
  • [39] Crack growth prediction for irradiated stainless steels under the combined fatigue-creep loading
    Fuller, Robert W.
    Simsiriwong, Jutima
    Shamsaei, Nima
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2020, 109
  • [40] DEFORMATION AND SUBCRITICAL CRACK-GROWTH UNDER STATIC LOADING
    YIN, H
    GAO, M
    WEI, RP
    JOURNAL OF METALS, 1988, 40 (07): : A55 - A55
12345