The oxidation of single-crystal nickel-based superalloys

被引：1
|
作者：
A. Akhtar
S. Hegde
R. C. Reed
机构：
[1] Department of Materials Engineering at the University of British Columbia in Vancouver,
[2] Department of Materials at Imperial College in London,undefined
来源：
JOM | 2006年 / 58卷
关键词：
NiAl; Bond Coat; Thermal Barrier Coating; Internal Oxidation; External Scale;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A phase transformation occurs in nickel-based single-crystal superalloys as a result of the oxidation that creates the external NiO scale. This transformation, which is the precursor to internal oxidation, creates the β phase (NiAl) first followed by the δ phase (Ni2Al3) prior to the formation of the spinel Ni (Cr, Al)2O4 and Al2O3 in succession. The implications of this effect on the rate of oxidation are discussed in this article.
引用
收藏
页码：37 / 42
页数：5
相关论文
共 50 条
  • [41] Mechanism of adding rhenium to improve hot corrosion resistance of nickel-based single-crystal superalloys
    Yang, Fang-Min
    Lian, Li-Xian
    Liu, Ying
    Gong, Xiu-Fang
    RARE METALS, 2021, 40 (08) : 2076 - 2082
  • [42] Very high cycle fatigue of nickel-based single-crystal and directionally solidified superalloys: Review
    Li Q.
    Zhang F.
    Zhao Z.
    Hangkong Xuebao/Acta Aeronautica et Astronautica Sinica, 2021, 42 (05):
  • [43] Influence of Process Parameter and Alloy Composition on Misoriented Eutectics in Single-Crystal Nickel-Based Superalloys
    Wittenzellner, Tobias
    Sumarli, Shieren
    Dai, Zijin
    Cocen, Ocson
    Schaar, Helge
    Wang, Fu
    Ma, Dexin
    Buehrig-Polaczek, Andreas
    MATERIALS, 2023, 16 (12)
  • [44] Microsegregation behavior of alloying elements in single-crystal nickel-based superalloys with emphasis on dendritic structure
    Wang, F.
    Ma, D.
    Buehrig-Polaczek, A.
    MATERIALS CHARACTERIZATION, 2017, 127 : 311 - 316
  • [45] Mechanism of adding rhenium to improve hot corrosion resistance of nickel-based single-crystal superalloys
    Fang-Min Yang
    Li-Xian Lian
    Ying Liu
    Xiu-Fang Gong
    RareMetals, 2021, 40 (08) : 2076 - 2082
  • [46] Creep prediction model for nickel-based single-crystal superalloys considering precipitation of TCP phase
    Xiao-Yan Wang
    Jia-Jia Wang
    Cheng-Jiang Zhang
    Wen-Wei Tong
    Bo Jiang
    Guang-Xian Lu
    Zhi-Xun Wen
    Tao Feng
    Rare Metals, 2021, 40 (10) : 2892 - 2904
  • [47] Investigation of grain competitive growth during directional solidification of single-crystal nickel-based superalloys
    Zhao, Xinbao
    Liu, Lin
    Zhang, Jun
    APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2015, 120 (02): : 793 - 800
  • [48] Mechanism of adding rhenium to improve hot corrosion resistance of nickel-based single-crystal superalloys
    Fang-Min Yang
    Li-Xian Lian
    Ying Liu
    Xiu-Fang Gong
    Rare Metals, 2021, 40 : 2076 - 2082
  • [49] On The Oxidation Resistance of Nickel-Based Superalloys
    Sato, Atsushi
    Moverare, Johan J.
    Hasselqvist, Magnus
    Reed, Roger C.
    EURO SUPERALLOYS 2010, 2011, 278 : 174 - +
  • [50] Precipitation and dissolution processes in γ/γ′ single crystal nickel-based superalloys
    Grosdidier, T
    Hazotte, A
    Simon, A
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 256 (1-2): : 183 - 196
12345