Magnetic properties of Dy(Tb)Co/Cr thin films for hybrid recording

被引：0
|
作者：
Z. Y. Lee
F. Jin
K. Wang
Z. X. Huang
Z. Li
X. M. Cheng
X. H. Xu
机构：
[1] Huazhong University of Science and Technology,Department of Solid State Electronics
[2] Central China Normal University,Department of Physics
来源：
Microsystem Technologies | 2007年 / 13卷
关键词：
Magnetic Layer; Argon Pressure; Apply Bias Voltage; Alloy Thin Film; Kerr Rotation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The magnetic properties of a DyCo layer with and without a Cr underlayer has been investigated. Optimal sputtering conditions of TbCo/Cr films for higher coercivity have been researched. Magnetron sputtering was used here to produce Cr/Dy(Tb)Cox/Cr films on glass substrates. It was found that both the magnetic and the Cr underlayer thickness could influence the coercivity of DyCo films. A coercivity as high as 3,500 Oe was obtained in 255 nm Dy31Co69 films with a 65 nm thick Cr underlayer, but it was only about 2,000 Oe for the same thickness Dy31Co69 films without Cr underlayer. The Cr underlayer thickness was varied in the range 16–330 nm to study its effect on magnetic properties in the films. Under optimal sputtering conditions, a coercivity as high as 6.5 kOe was obtained in TbCo/Cr films. The results indicate that Cr underlayers are suitable for DyCo layers in order to increase the coercivity and the Dy(Tb)Co/Cr film are good candidates for high density recording media.
引用
收藏
页码：165 / 168
页数：3
相关论文
共 50 条
  • [41] Magnetic and recording properties of amorphous TbFeCo-In thin films
    Raasch, D
    JOURNAL OF APPLIED PHYSICS, 1996, 80 (05) : 2964 - 2967
  • [42] The Influence of Underlayers on the Magnetic Properties of TbFeCo Films for Hybrid Recording
    Cheng, Weiming
    Miao, Xiangshui
    Yan, Junbing
    Lin, Gengqi
    EIGHTH INTERNATIONAL SYMPOSIUM ON OPTICAL STORAGE AND 2008 INTERNATIONAL WORKSHOP ON INFORMATION DATA STORAGE, 2009, 7125
  • [43] MAGNETIC, RECORDING AND STRUCTURAL CHARACTERISTICS OF SPUTTERED CO-CR-PT FILMS FOR LONGITUDINAL RECORDING
    LIN, T
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1990, 86 (2-3) : 159 - 168
  • [44] Structure and magnetic properties of nanocomposite (Nd, Dy)-(Fe, Co)-B/α-Fe thin films with perpendicular magnetic anisotropy
    Yao, Q.
    Liu, W.
    Cui, W. B.
    Yang, F.
    Zhao, X. G.
    Zhang, Z. D.
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2009, 42 (03)
  • [45] Magnetic and transport properties of Py/Cr/Co/Cr sputtered films
    Lo, C.K.
    Klik, I.
    Ho, C.H.
    Chang, C.J.
    Liou, Y.
    Yao, Y.D.
    IEEE Transactions on Magnetics, 1997, 33 (5 pt 2): : 3526 - 3528
  • [46] Magnetic and transport properties of Py/Cr/Co/Cr sputtered films
    Lo, CK
    Klik, I
    Ho, CH
    Chang, CJ
    Liou, Y
    Yao, YD
    IEEE TRANSACTIONS ON MAGNETICS, 1997, 33 (05) : 3526 - 3528
  • [47] EFFECT OF ANNEALING ON CRYSTALLINE STATE AND MAGNETIC PROPERTIES OF (Tb0.28Dy0.72) Fe1.90 THIN FILMS
    Li, Kuoshe
    Li, Hongwei
    Yan, Hui
    Yu, Dunbo
    Wang, Fengying
    Zhang, Guocheng
    INTERNATIONAL JOURNAL OF MODERN PHYSICS B, 2009, 23 (6-7): : 1841 - 1846
  • [48] Magnetic order of Cr thin films in Nb/Cr/Fe-nanoisland hybrid: A comparative study between magnetic and superconducting properties
    Navarro, E.
    Velez, M.
    Huttel, Y.
    Junquera, A. Perez
    Martin, J. I.
    de Lima, O. F.
    Cebollada, A.
    Alameda, J. M.
    Vicent, J. L.
    JOURNAL OF APPLIED PHYSICS, 2009, 105 (03)
  • [49] THE INFLUENCE OF THE TEXTURAL DEVELOPMENT ON MAGNETIC-PROPERTIES IN CO-CR THIN-FILMS
    LI, CZ
    LODDER, JC
    SZPUNAR, JA
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1994, 131 (03) : 427 - 439
  • [50] Magnetic properties of nanocrystalline Fe-Co(Cr)-Hf-N thin films
    Kim, K.H.
    Kim, Y.H.
    Kim, J.
    Han, S.H.
    Kim, H.J.
    1600, Am Inst Phys, Woodbury, NY, USA (87):
12345