Changes in the Electrochemical Characteristics of Corrosion-Resistant Steels at the Beginning of the Process of Corrosion-Fatigue Damage

被引：0
|
作者：
M. S. Khoma
V. I. Pokhmurs'kyi
机构：
[1] Ukrainian Academy of Sciences,Karpenko Physicomechanical Institute
来源：
Materials Science | 2003年 / 39卷
关键词：
Fatigue; Stainless Steel; Crack Initiation; Analytic Relation; Relative Strain;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
We establish the relationship between the electrochemical characteristics of the stage of crack initiation and the susceptibility of various types of stainless steels to corrosion fatigue and show that the proposed parameter of relative strain fracture can be used as a criterion of corrosion-fatigue fracture of steels caused by the accelerated dissolution of microstrained regions on their surface. We also deduce analytic relations for the evaluation of the corrosion-fatigue limit of passivated steels. The accuracy of the proposed formulas is never worse than 12%.
引用
收藏
页码：1 / 7
页数：6
相关论文
共 50 条
12345