Transformation of defects in continuous-cast billet during rail production

被引：0

作者：

Yur'ev A.B. ^{[1
]}

Godik L.A. ^{[1
]}

Kozyrev N.A. ^{[1
]}

Korneva L.V. ^{[1
]}

Boikov D.V. ^{[1
]}

机构：

[1] OAO Novokuznetskii Metallurgicheskii Kombinat (NKMK), Novokuznetsk

来源：

Steel in Translation | 2009年 / 39卷 / 7期

关键词：

Nonmetallic Inclusion; Longitudinal Crack; Slag Inclusion; Cold Crack; Corner Crack;

D O I：

10.3103/S0967091209070134

中图分类号：

学科分类号：

摘要：

Defects of continuous-cast billet and their transformation at different stages of rail production are studied. It is found that, on many occasions. longitudinal surface cracks in the billet (of shrinkage or groove type) do not lead to the formation of surface defects on rails, whereas crystallization cracks accompanied by slag inclusions or closure of the metal may be transformed to rolling cracks or blisters on rolling. © Allerton Press, Inc., 2009.

引用

页码：573 / 575

页数：2

共 50 条

[31] Temperature Fields and Thermal Stress in the Solidification of Cylindrical Continuous-Cast Steel Billet
Krayushkin N.A.
Pribytkov I.A.
Shatokhin K.S.
Steel in Translation, 2019, 49 (01): : 20 - 23
[32] Centering of continuous-cast billet prior to piercing at OAO Severskii Trubnyi Zavod
Kuryatnikov A.V.
Korol’ A.V.
Toporov V.A.
Stepanov A.I.
Panasenko O.A.
Steel in Translation, 2014, 44 (06) : 456 - 459
[33] New methods of rolling and straightening rails from continuous-cast billet at OAO NKMK
Dorofeev S.V.
Dorofeev V.V.
Yur'Ev A.B.
Peretyat'Ko V.N.
Gromov V.E.
Steel in Translation, 2008, 38 (12) : 973 - 975
[34] Deformation of Continuous-Cast Metal During Rotary Rolling
A. N. Nikulin
V. V. Streletskii
Metallurgist, 2005, 49 : 97 - 101
[35] Deformation of continuous-cast metal during rotary rolling
Nikulin, AN
Streletskii, VV
METALLURGIST, 2005, 49 (3-4) : 97 - 101
[36] Deformation of continuous-cast metal during rotary rolling
Nikulin, A.N.
Streletskii, V.V.
Metallurg, 2005, (03): : 43 - 46
[37] Alleviating defects in continuous-cast ingots by inserting vortex suppressors in the tundish
Kuklev, AV
Tinyakov, NV
Aizin, YM
Gushchin, VN
Ul'yanov, VA
METALLURGIST, 2004, 48 (5-6) : 207 - 209
[38] More economical heating of continuous-cast 60C2XA steel billet in continuous furnaces
Temlyantsev M.V.
Konoz K.S.
Dziuba A.Y.
Umanskii A.A.
Temlyantsev N.V.
Steel in Translation, 2015, 45 (8) : 539 - 542
[39] Macrostructure of hot-pressed boiler pipe made from undeformed continuous-cast billet
Opryshko L.V.
Lube I.I.
Suponin A.G.
Steel in Translation, 2008, 38 (8) : 694 - 696
[40] Determining the thermal state of the surface of continuous-cast billet using charge-coupled devices
Kazachkov E.A.
Fedosov A.V.
Chichkarev E.A.
Kislitsa V.V.
Isaev O.B.
Steel Transl., 2009, 12 (1039-1042): : 1039 - 1042

← 1 2 3 4 5 →