Oxidation Behavior of the Single-Crystal Ni-base Superalloy DD32 in Air at 900, 1000, and 1100°C

被引：1
|
作者：
L. Huang
X. F. Sun
H. R. Guan
Z. Q. Hu
机构：
[1] Chinese Academy of Sciences,State Key Laboratory for Corrosion and Protection, Institute of Metal Research
来源：
Oxidation of Metals | 2006年 / 65卷
关键词：
single-crystal Ni-base superalloy; DD32; oxidation; kinetics; microstructure;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The isothermal-oxidation behavior of the single-crystal Ni-base superalloy DD32 was studied over the temperature range from 900–1100 °C and analyzed by OM, TGA, XRD, EDX, SED, and EPMA. The alloy DD32 obeyed a subparabolic rate law during oxidation at 900 and 1000°C, while the alloy showed a rather high oxidation rate at 1100°C. The severe composition segregation, which resulted from the solidification process, led to the formation of different scale on the dendritic and interdendritic regions. Internal nitride (AlN) was observed in the subsurface zone of dendritic areas, but absent in interdendritic areas. The oxidation mechanism of the alloy DD32 is discussed by comparing with other alloys.
引用
收藏
页码：391 / 408
页数：17
相关论文
共 50 条
  • [11] Oxidation behavior of a single-crystal Ni-base superalloy in air at 900 and 1050 °C
    Xudong Lu
    Sugui Tian
    Xingfu Yu
    Changxin Wang
    Rare Metals, 2011, 30 : 439 - 442
  • [12] Oxidation behavior of a single-crystal Ni-base superalloy in air at 900 and 1050 °C
    Lu Xudong
    Tian Sugui
    Yu Xingfu
    Wang Changxin
    RARE METALS, 2011, 30 : 439 - 442
  • [13] Oxidation behavior of a Single-crystal Ni-base superalloy in air.: I:: At 800 and 900°C
    Li, MH
    Sun, XF
    Li, JG
    Zhang, ZY
    Jin, T
    Guan, HR
    Hu, ZQ
    OXIDATION OF METALS, 2003, 59 (5-6): : 591 - 605
  • [14] Oxidation Behavior of a Single-Crystal Ni-Base Superalloy in Air. I: At 800 and 900°C
    M.H. Li
    X.F. Sun
    J.G. Li
    Z.Y. Zhang
    T. Jin
    H.R. Guan
    Z.Q. Hu
    Oxidation of Metals, 2003, 59 : 591 - 605
  • [15] Isothermal Oxidation Behavior Characteristics of a Second Generation Ni-base Single Crystal Superalloy in Air at 1000 and 1100°C
    Latief, Fahamsyah H.
    Kakehi, Koji
    Fu, Xintao
    Tashiro, Yuma
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2012, 7 (09): : 8369 - 8383
  • [16] Oxidation Behavior of a Cast Polycrystalline Ni-Base Superalloy in Air: At 900 and 1000 °C
    H. Wei
    G. C. Hou
    X. F. Sun
    H. R. Guan
    Z. Q. Hu
    Oxidation of Metals, 2007, 68 : 149 - 163
  • [17] Oxidation behavior of a cast polycrystalline Ni-base superalloy in air:: At 900 and 1000 °C
    Wei, H.
    Hou, G. C.
    Sun, X. F.
    Guan, H. R.
    Hu, Z. Q.
    OXIDATION OF METALS, 2007, 68 (3-4): : 149 - 163
  • [18] Isothermal oxidation behavior of single-crystal Ni-base superalloy containing rhenium in air
    Chunting, Liu
    Xiaofeng, Sun
    Ji, Ma
    Haiyan, Cong
    Wanfeng, Liu
    RARE METAL MATERIALS AND ENGINEERING, 2007, 36 (08) : 1407 - 1411
  • [19] Microstructure and tensile properties of DD32 single crystal Ni-base superalloy repaired by laser metal forming
    Shiwei Ci
    Jingjing Liang
    Jinguo Li
    Yizhou Zhou
    Xiaofeng Sun
    JournalofMaterialsScience&Technology, 2020, 45 (10) : 23 - 34
  • [20] Effect of heat treatment on microstructure and stress rupture life of DD32 single crystal Ni-base superalloy
    Yu Jinjiang
    Sun Xiaofeng
    Zhao Nairen
    Jin Tao
    Guan Hengrong
    Hu Zhuangqi
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 460 : 420 - 427
12345