Oxidation Behavior of the Single-Crystal Ni-base Superalloy DD32 in Air at 900, 1000, and 1100°C

被引：1
|
作者：
L. Huang
X. F. Sun
H. R. Guan
Z. Q. Hu
机构：
[1] Chinese Academy of Sciences,State Key Laboratory for Corrosion and Protection, Institute of Metal Research
来源：
Oxidation of Metals | 2006年 / 65卷
关键词：
single-crystal Ni-base superalloy; DD32; oxidation; kinetics; microstructure;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The isothermal-oxidation behavior of the single-crystal Ni-base superalloy DD32 was studied over the temperature range from 900–1100 °C and analyzed by OM, TGA, XRD, EDX, SED, and EPMA. The alloy DD32 obeyed a subparabolic rate law during oxidation at 900 and 1000°C, while the alloy showed a rather high oxidation rate at 1100°C. The severe composition segregation, which resulted from the solidification process, led to the formation of different scale on the dendritic and interdendritic regions. Internal nitride (AlN) was observed in the subsurface zone of dendritic areas, but absent in interdendritic areas. The oxidation mechanism of the alloy DD32 is discussed by comparing with other alloys.
引用
收藏
页码：391 / 408
页数：17
相关论文
共 50 条
  • [1] Oxidation behavior of the single-crystal Ni-base superalloy DD32 in air at 900, 1000, and 1100°C
    Huang, L.
    Sun, X. F.
    Guan, H. R.
    Hu, Z. Q.
    OXIDATION OF METALS, 2006, 65 (5-6): : 391 - 408
  • [2] Oxidation of the single-crystal Ni-base superalloy DD32 containing rhenium in air at 900 and 1000 °C
    Liu, CT
    Sun, XF
    Guan, HR
    Hu, ZQ
    SURFACE & COATINGS TECHNOLOGY, 2005, 197 (01): : 39 - 44
  • [3] Oxidation Behavior of a Single-Crystal Ni-base Superalloy in Air at 900, 1000 and 1100°C
    L. Huang
    X. F. Sun
    H. R. Guan
    Z. Q. Hu
    Oxidation of Metals, 2006, 65 : 207 - 222
  • [4] Oxidation behavior of a single-crystal Ni-base superalloy in air at 900, 1000 and 1100 °C
    Huang, L.
    Sun, X. F.
    Guan, H. R.
    Hu, Z. Q.
    TRIBOLOGY LETTERS, 2006, 23 (01) : 15 - 22
  • [5] Oxidation behavior of a single-crystal Ni-base superalloy in air at 900, 1000 and 1100°C
    Huang, L.
    Sun, X. F.
    Guan, H. R.
    Hu, Z. Q.
    OXIDATION OF METALS, 2006, 65 (3-4): : 207 - 222
  • [6] Oxidation behavior of a single-crystal Ni-base superalloy in air at 900, 1000 and 1100 °C
    L. Huang
    X.F. Sun
    H.R. Guan
    Z.Q. Hu
    Tribology Letters, 2006, 23 : 15 - 22
  • [7] Oxidation behavior of a single-crystal Ni-base superalloy in air at 900, 1000 and 1100 °C
    L. Huang
    X. F. Sun
    H. R. Guan
    Z. Q. Hu
    Tribology Letters, 2007, 27 (1) : 127 - 127
  • [8] Oxidation behavior of a single-crystal Ni-base superalloy between 900 and 1000°C in air
    Liu, C. T.
    Ma, J.
    Sun, X. F.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 491 (1-2) : 522 - 526
  • [9] Oxidation Behavior of a Single-Crystal Ni-Base Superalloy in Air—II: At 1000, 1100, and 1150°C
    M.H. Li
    X.F. Sun
    T. Jin
    H.R. Guan
    Z.Q. Hu
    Oxidation of Metals, 2003, 60 : 195 - 210
  • [10] Oxidation behavior of a single-crystal Ni-base superalloy in air -: II:: At 1000, 1100, and 1150°C
    Li, MH
    Sun, XF
    Jin, T
    Guan, HR
    Hu, ZQ
    OXIDATION OF METALS, 2003, 60 (1-2): : 195 - 210
12345