Transparent Nd3+-Activated Glass-Ceramics in the Li2O–Al2O3–SiO2System: Physicochemical Aspects of Their Preparation and Optical Characteristics

The spectral–optical properties of transparent neodymium-activated lithium aluminosilicate glass-ceramics with titanium dioxide as a crystallization catalyst are investigated. The compositions of the initial glasses and the temperature–time schedules of heat treatment that provide a way of preparing highly homogeneous samples with low optical losses are determined. The most important parameters characterizing emission from the 4F3/2metastable state of neodymium ions are obtained by analyzing the optical spectra of rare-earth ions in terms of the Judd–Ofelt theory. It is shown that the introduction of phosphorus oxide into the composition of glass-ceramics leads to a considerable increase in the stimulated emission cross section for the basic 4F3/2–4I11/2transition, even though the rare-earth activator is not incorporated into the crystalline phase. It is found that acceptable quantum yields of fluorescence with the retention of a high heat resistance of glass-ceramics can be achieved by decreasing the volume fraction of the crystalline phase. The lasing testing of the materials prepared is performed in a setup with a lamp pumping. The low lasing parameters can be associated with the specific features in the optical properties of glass-ceramics, primarily, with the revealed depolarization of polarized light due to the presence of microstresses at interfaces.