Electrical resistivity and magnetoresistive behaviour of bismuth-substituted lanthanum manganites La0.4Bi0.1Ca0.5−xSrxMnO3 (x = 0.1 and 0.2) were systematically studied by varying the temperature from 2 to 300 K and the magnetic field up to 12 T. The samples were found to crystallize in rhombohedral structure and their morphology shows near-spherical nanosize crystallites. Charge ordering was observed in both the samples under zero field conditions and corresponding transition temperature TCO was found to decrease with the increase of x. Resistivity measurements with magnetic field also showed suppression of magnetoresistivity (MR) with the increase of x and the maximum MR was found to be 98 and 93% for x = 0.1 and 0.2, respectively, at 10 T. In the high-temperature domain, the electronic transport was observed to be dominated by the variable range hopping mechanism for both the samples, whereas in the low-temperature domain the electrical conduction of x = 0.1 sample was observed to be contributed by various other electron scattering mechanisms.
机构:
School of Materials Engineering, YanCheng Institute of Technology, YanCheng,224051, ChinaSchool of Materials Engineering, YanCheng Institute of Technology, YanCheng,224051, China
Shi, Xinlu
Wen, Yongchun
论文数: 0引用数: 0
h-index: 0
机构:
School of Materials Engineering, YanCheng Institute of Technology, YanCheng,224051, ChinaSchool of Materials Engineering, YanCheng Institute of Technology, YanCheng,224051, China
Wen, Yongchun
Gu, Daguo
论文数: 0引用数: 0
h-index: 0
机构:
School of Materials Engineering, YanCheng Institute of Technology, YanCheng,224051, ChinaSchool of Materials Engineering, YanCheng Institute of Technology, YanCheng,224051, China
Gu, Daguo
Hou, Haijun
论文数: 0引用数: 0
h-index: 0
机构:
School of Materials Engineering, YanCheng Institute of Technology, YanCheng,224051, ChinaSchool of Materials Engineering, YanCheng Institute of Technology, YanCheng,224051, China
Hou, Haijun
Zhang, Yaheng
论文数: 0引用数: 0
h-index: 0
机构:
School of Materials Engineering, YanCheng Institute of Technology, YanCheng,224051, ChinaSchool of Materials Engineering, YanCheng Institute of Technology, YanCheng,224051, China
Zhang, Yaheng
Wang, Cong
论文数: 0引用数: 0
h-index: 0
机构:
Center of Condensed Matter and Materials Physics, Department of Physics, Beihang University, Beijing,100191, ChinaSchool of Materials Engineering, YanCheng Institute of Technology, YanCheng,224051, China