Multicycle Fatigue of Single Crystal Nickel Superalloy

被引：0
|
作者：
M. S. Belyaev
M. R. Orlov
机构：
[1] State Research Center of the Russian Federation – All-Russia Research Institute of Aviation Materials,
来源：
Metallurgist | 2018年 / 62卷
关键词：
single crystal nickel-base superalloy; crystallographic orientation; multicycle fatigue; fractographic analysis; scanning electron microscopy;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Multicycle fatigue of an experimental low-alloy single-crystal nickel-base superalloy is studied in relation to crystal orientation and test temperature. It is established that with an increase in test temperature from 20 to 900°C a change is observed in the shape of the multicycle fatigue curve. Scanning electron microscopy is used to determine the nature of fatigue failure. The work was conducted within the scope of a priority area for development of RF science, technology, and engineering, i.e., transport and space systems.
引用
收藏
页码：70 / 77
页数：7
相关论文
共 50 条
  • [41] Transient thermal fatigue crack propagation behavior of a nickel-based single-crystal superalloy
    Pei, Haiqing
    Wen, Zhixun
    Wang, Zhaohan
    Gan, Wenyan
    Lu, Guang Xian
    Yue, Zhufeng
    INTERNATIONAL JOURNAL OF FATIGUE, 2020, 131
  • [42] Interaction of hot corrosion fatigue and load dwell periods on a nickel-base single crystal superalloy
    Brooking, L.
    Gray, S.
    Sumner, J.
    Nicholls, J. R.
    Simms, N. J.
    INTERNATIONAL JOURNAL OF FATIGUE, 2018, 117 : 13 - 20
  • [43] Characterization of deformation mechanisms during low cycle fatigue of a single crystal nickel-based superalloy
    Hong, H. U.
    Choi, B. G.
    Kim, I. S.
    Yoo, Y. S.
    Jo, C. Y.
    JOURNAL OF MATERIALS SCIENCE, 2011, 46 (15) : 5245 - 5251
  • [44] Deformation behavior during thermo-mechanical fatigue of a nickel-based single crystal superalloy
    Hong, H. U.
    Choi, B. G.
    Kim, I. S.
    Yoo, Y. S.
    Jo, C. Y.
    11TH INTERNATIONAL CONFERENCE ON THE MECHANICAL BEHAVIOR OF MATERIALS (ICM11), 2011, 10
  • [45] Temperature Dependence on Cracking Behavior in Thermomechanical Fatigue of Nickel-Based Single-Crystal Superalloy
    Dao, Van Hung
    Yun, Hee Soo
    Jeon, Sang Koo
    Park, Jaeyeong
    Nahm, Seung Hoon
    METALS AND MATERIALS INTERNATIONAL, 2025,
  • [46] Thermal-Mechanical Fatigue Behavior and Life Assessment of Single Crystal Nickel-Based Superalloy
    Cao, Juan
    Jing, Fulei
    Yang, Junjie
    CRYSTALS, 2023, 13 (05)
  • [47] A comparative study on thermomechanical and low cycle fatigue failures of a single crystal nickel-based superalloy
    Hong, H. U.
    Kang, J. G.
    Choi, B. G.
    Kim, I. S.
    Yoo, Y. S.
    Jo, C. Y.
    INTERNATIONAL JOURNAL OF FATIGUE, 2011, 33 (12) : 1592 - 1599
  • [48] Dislocation Structure in a Single Crystal Nickel Base Superalloy During High Cycle Fatigue at 870 °C
    Shui Li
    Xu Yunchao
    Hu Zhuangqi
    RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (04) : 1054 - 1058
  • [49] A FRACTOGRAPHIC STUDY OF STAGE-1 FATIGUE CRACKING IN A NICKEL-BASE SUPERALLOY SINGLE CRYSTAL
    DUQUETTE, DJ
    GELL, M
    PITEO, JW
    METALLURGICAL TRANSACTIONS, 1970, 1 (11): : 3107 - &
  • [50] Fatigue life prediction model based on critical plane of nickel-based single crystal superalloy
    Wang, Rong-Qiao
    Jing, Fu-Lei
    Hu, Dian-Yin
    Hangkong Dongli Xuebao/Journal of Aerospace Power, 2013, 28 (11): : 2587 - 2592
12345