On concentration galvanic elements in corrosion-mechanical cracks

被引：0
|
作者：
L. N. Petrov
V. G. Zakharchuk
K. Sulek
B. Szczegelnjak
机构：
来源：
Materials Science | 1999年 / 35卷
关键词：
Model Condition; Structural Material; Corrosion Process; Operation Condition; Corrosive Medium;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Under model conditions, we establish the influence of the composition of a corrosive medium on the functioning of short-circuit galvanic elements that determine the corrosion pitting of cracks under stress. We show that, depending on the operation conditions, galvanic elements can lead both to localization and to delocalization of corrosion processes near the crack tip.
引用
收藏
页码：232 / 236
页数：4
相关论文
共 50 条
  • [21] Equipment for corrosion-mechanical tests in actual conditions
    Kushnarenko, V.M.
    Fot, A.P.
    Uzyakov, R.N.
    Industrial Laboratory (USSR) (English translation of Zavodskaya Laboratoriya), 1992, 57 (07):
  • [22] EQUIPMENT FOR CORROSION-MECHANICAL TESTS IN ACTUAL CONDITIONS
    KUSHNARENKO, VM
    FOT, AP
    UZYAKOV, RN
    INDUSTRIAL LABORATORY, 1991, 57 (07): : 742 - 743
  • [23] ON THE NATURE OF CORROSION-MECHANICAL WEAR OF METALS.
    Preis, G.A.
    Soviet Journal of Friction and Wear (English translation of Trenie i Iznos), 1987, 8 (05): : 16 - 20
  • [24] A DEFORMATION CRITERION OF THE ONSET OF CORROSION-MECHANICAL DAMAGE
    STEKLOV, OI
    POLYARUS, AN
    PROTECTION OF METALS, 1980, 16 (05): : 437 - 441
  • [25] Corrosion-mechanical fracture of tube steels in operation
    Ioffe, A. V.
    Tetyueva, T. V.
    Revyakin, V. A.
    Borisenkova, E. A.
    Knyaz'kin, S. A.
    Denisova, T. V.
    METAL SCIENCE AND HEAT TREATMENT, 2013, 54 (9-10) : 512 - 518
  • [26] Equipment and method of steel and alloys corrosion-mechanical test
    Livshits, L.S.
    Kushekov, A.U.
    Levin, S.M.
    Zavodskaya Laboratoriya, 1992, 58 (02):
  • [27] Corrosion-Mechanical Wear of Nitrided Steels in Acidic Medium
    Stechyshyn, M. S.
    Stechyshyna, N. M.
    Dykha, O. V.
    Martynyuk, A. V.
    Liukhovets, V. V.
    Lukyanyuk, M. V.
    MATERIALS SCIENCE, 2023, 58 (05) : 597 - 601
  • [28] Equipment and method for autoclave corrosion-mechanical and electrochemical investigations
    Antoshchak, IM
    Gnyp, IP
    MATERIALS SCIENCE, 2000, 36 (03) : 392 - 400
  • [29] CORROSION-MECHANICAL FATIGUE - THE DIRECT AND INVERSE EFFECTS (SURVEY)
    SOSNOVSKII, LA
    MAKHUTOV, NA
    INDUSTRIAL LABORATORY, 1993, 59 (07): : 678 - 695
  • [30] Identification of corrosion-mechanical fracture mechanism of structural steels
    Nykyforchyn, HM
    Tsyrulnyk, OT
    ECF 12: FRACTURE FROM DEFECTS, VOLS. I-III, 1998, : 1193 - 1198
12345