Influence of the Matrix Type on the Mode I Fracture of Carbon-Epoxy Composites Under Dynamic Delamination

被引：0
|
作者：
A. Argüelles
J. Viña
A. F. Canteli
A. Lopez
机构：
[1] University of Oviedo,Department of Construction and Manufacturing Engineering
[2] University de Oviedo,Department of Materials Science and Metallurgical Engineering
来源：
Experimental Mechanics | 2011年 / 51卷
关键词：
Delamination; Mode I; Fracture; Fatigue; Matrix;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The delamination energy and fracture behaviour under static and dynamic mode I loading of two composites, made of the same unidirectional carbon reinforcement embedded in two different matrices, one tough and the other brittle, was investigated with the aim of analyzing the influence of the employed resin on the fatigue delamination behaviour of both composites. In the case of dynamic loading, the number of cycles necessary for the onset of delamination was determined for a given elastic energy release rate and crack growth rate for different critical energy rates. The double cantilever beam (DCB) test was found to be suitable for promoting the initial delamination. The experimental results confirm the enhanced performance of the tough resin both in terms of crack initiation and growth rate.
引用
收藏
页码：293 / 301
页数：8
相关论文
共 50 条
  • [41] MIXED-MODE DELAMINATION BEHAVIOR OF CARBON/EPOXY COMPOSITES
    ZHAO, S
    GADKE, M
    PRINZ, R
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 1995, 14 (08) : 804 - 826
  • [42] Influence of loading rate on the delamination response of untufted and tufted carbon epoxy non crimp fabric composites: Mode I
    de Verdiere, M. Colin
    Skordos, A. A.
    May, M.
    Walton, A. C.
    ENGINEERING FRACTURE MECHANICS, 2012, 96 : 11 - 25
  • [43] Dynamic aspects of the lattice structures behavior in the manufacturing of carbon-epoxy composites
    Golfman, Y., 1600, Soc. for the Advancement of Material and Process Engineering (35):
  • [44] The Influence of Carbon/Glass/Epoxy Hybrid Interfacial Adhesion on the Mode II Delamination Fracture Toughness
    F. M. Monticeli
    H. L. Ornaghi
    M. O. H. Cioffi
    H. J. C. Voorwald
    Mechanics of Composite Materials, 2022, 58 : 237 - 248
  • [45] The Influence of Carbon/Glass/Epoxy Hybrid Interfacial Adhesion on the Mode II Delamination Fracture Toughness
    Monticeli, F. M.
    Ornaghi, H. L., Jr.
    Cioffi, M. O. H.
    Voorwald, H. J. C.
    MECHANICS OF COMPOSITE MATERIALS, 2022, 58 (02) : 237 - 248
  • [46] Dynamic aspects of the lattice structures behavior in the manufacturing of carbon-epoxy composites
    Golfman, Y
    JOURNAL OF ADVANCED MATERIALS, 2003, 35 (02): : 3 - 8
  • [47] Mode I interlaminar fracture toughness of woven glass/epoxy composites with mat layers at delamination interface
    Hosseini, Mohammad Reza
    Taheri-Behrooz, Fathollah
    Salamat-talab, Mazaher
    POLYMER TESTING, 2019, 78
  • [48] Mixed-mode delamination fracture toughness of unidirectional glass/epoxy composites under fatigue loading
    Kenane, M
    Benzeggagh, ML
    COMPOSITES SCIENCE AND TECHNOLOGY, 1997, 57 (05) : 597 - 605
  • [49] Repairing wood beams under bending using carbon-epoxy composites
    Dourado, N.
    Pereira, F. A. M.
    de Moura, M. F. S. F.
    Morais, J. J. L.
    ENGINEERING STRUCTURES, 2012, 34 : 342 - 350
  • [50] Influence of Resin Type on the Delamination Behavior of Carbon Fiber Reinforced Composites Under Mode-II Loading
    Argueelles, A.
    Vina, J.
    Canteli, A. F.
    Bonhomme, J.
    INTERNATIONAL JOURNAL OF DAMAGE MECHANICS, 2011, 20 (07) : 963 - 978
12345