Influence of the Matrix Type on the Mode I Fracture of Carbon-Epoxy Composites Under Dynamic Delamination

被引：0
|
作者：
A. Argüelles
J. Viña
A. F. Canteli
A. Lopez
机构：
[1] University of Oviedo,Department of Construction and Manufacturing Engineering
[2] University de Oviedo,Department of Materials Science and Metallurgical Engineering
来源：
Experimental Mechanics | 2011年 / 51卷
关键词：
Delamination; Mode I; Fracture; Fatigue; Matrix;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The delamination energy and fracture behaviour under static and dynamic mode I loading of two composites, made of the same unidirectional carbon reinforcement embedded in two different matrices, one tough and the other brittle, was investigated with the aim of analyzing the influence of the employed resin on the fatigue delamination behaviour of both composites. In the case of dynamic loading, the number of cycles necessary for the onset of delamination was determined for a given elastic energy release rate and crack growth rate for different critical energy rates. The double cantilever beam (DCB) test was found to be suitable for promoting the initial delamination. The experimental results confirm the enhanced performance of the tough resin both in terms of crack initiation and growth rate.
引用
收藏
页码：293 / 301
页数：8
相关论文
共 50 条
  • [1] Influence of the Matrix Type on the Mode I Fracture of Carbon-Epoxy Composites Under Dynamic Delamination
    Argueelles, A.
    Vina, J.
    Canteli, A. F.
    Lopez, A.
    EXPERIMENTAL MECHANICS, 2011, 51 (03) : 293 - 301
  • [2] Study of the influence of the type of matrix used in carbon-epoxy composites on fatigue delamination under mode III fracture
    Bertorello, C.
    Vina, J.
    Vina, I.
    Arguelles, A.
    MATERIALS & DESIGN, 2020, 186
  • [3] Influence of temperature on the delamination process under mode I fracture and dynamic loading of two carbon-epoxy composites
    Argueelles, A.
    Vina, J.
    Canteli, A. F.
    Coronado, P.
    Mollon, V.
    COMPOSITES PART B-ENGINEERING, 2015, 68 : 207 - 214
  • [4] Using a statistical model for the analysis of the influence of the type of matrix carbon-epoxy composites on the fatigue delamination under modes I and II of fracture
    Argueelles, A.
    Coronado, P.
    Canteli, A. F.
    Vina, J.
    Bonhomme, J.
    INTERNATIONAL JOURNAL OF FATIGUE, 2013, 56 : 54 - 59
  • [5] Influence of the Loading System on Mode I Delamination Results in Carbon-Epoxy Composites
    Vina, J.
    Argueelles, A.
    Lopez, A.
    Mollon, V.
    Bonhomme, J.
    EXPERIMENTAL TECHNIQUES, 2014, 38 (01) : 53 - 58
  • [6] Influence of the loading system on mode I delamination results in Carbon-Epoxy composites
    J. Viña
    A. Argüelles
    A. López
    V. Mollón
    J. Bonhomme
    Experimental Techniques, 2014, 38 : 53 - 58
  • [7] Influence of the Matrix Toughness in Carbon-Epoxy Composites Subjected to Delamination under Modes I, II, and Mixed I/II
    Bonhomme, J.
    Vina, J.
    Argueelles, A.
    Vina, I.
    Mollon, V.
    MECHANICS OF ADVANCED MATERIALS AND STRUCTURES, 2013, 20 (08) : 679 - 686
  • [8] Dependance of stress ratio on the Mode I fatigue delamination growth in woven carbon-epoxy composites
    Torres, Mauricio
    Sugey Garcia-Rivera, S.
    Rivas-Lopez, Diego
    Gonzalez-Velazquez, Jorge L.
    ADVANCES IN POLYMER TECHNOLOGY, 2018, 37 (08) : 3854 - 3860
  • [9] Influence of low temperatures on the phenomenon of delamination of mode I fracture in carbon-fibre/epoxy composites under fatigue loading
    Coronado, P.
    Argueelles, A.
    Vina, J.
    Vina, I.
    COMPOSITE STRUCTURES, 2014, 112 : 188 - 193
  • [10] Study of the phenomenon of fatigue delamination in a carbon-epoxy composite under mixed mode I/II fracture employing an asymmetric specimen
    Rubiera, S.
    Arguelles, A.
    Vina, J.
    Rocandio, C.
    INTERNATIONAL JOURNAL OF FATIGUE, 2018, 114 : 74 - 80
12345