Corrosion-mechanical fracture of tubing from carbon and alloy steels operating in environments containing hydrogen sulfide

被引：0
|
作者：
A. V. Ioffe
T. V. Tetyueva
M. A. Vyboishchik
S. A. Knyaz’kin
A. O. Zyryanov
机构：
[1] Samara Engineering-Technical Center,
[2] Tolyatti State University,undefined
来源：
Metal Science and Heat Treatment | 2013年 / 54卷
关键词：
sulfide stress corrosion cracking; tubing; field tests;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Comparative analysis of processes of corrosion-mechanical fracture of carbon and alloy steels in environments containing hydrogen sulfide is performed after laboratory (NACE TM0177) and field tests. The mechanism and kinetics of the evolution of fracture in steels of the two groups are considered.
引用
收藏
页码：492 / 497
页数：5
相关论文
共 50 条
  • [31] Stages of multiple fracture of low-alloy steels in a hydrogen sulfide medium
    Botvina, LR
    Tetyueva, TV
    Ioffe, AV
    METAL SCIENCE AND HEAT TREATMENT, 1998, 40 (1-2) : 61 - 70
  • [32] Stages of multiple fracture of low-alloy steels in a hydrogen sulfide medium
    L. R. Botvina
    T. V. Tetyueva
    A. V. Ioffe
    Metal Science and Heat Treatment, 1998, 40 : 61 - 70
  • [33] On the protection of carbon steels from hydrogen-sulfide corrosion with mixtures of volatile and contact inhibitors
    Kuznetsov, Yu. I.
    Frolova, L. V.
    Tomina, E. V.
    PROTECTION OF METALS, 2007, 43 (02): : 149 - 154
  • [34] On the protection of carbon steels from hydrogen-sulfide corrosion with mixtures of volatile and contact inhibitors
    Yu. I. Kuznetsov
    L. V. Frolova
    E. V. Tomina
    Protection of Metals, 2007, 43 : 149 - 154
  • [35] Corrosion of alloy steels containing 2% chromium in CO2 environments
    Guo, Shaoqiang
    Xu, Lining
    Zhang, Lei
    Chang, Wei
    Lu, Minxu
    CORROSION SCIENCE, 2012, 63 : 246 - 258
  • [36] CATALYTIC DISSOCIATION OF HYDROGEN-SULFIDE IN ABRASION CORROSION AND EROSION WEAR OF STEELS IN HYDROGEN-SULFIDE CONTAINING MEDIA
    KUCHER, LO
    SOVIET MATERIALS SCIENCE, 1989, 25 (01): : 51 - 54
  • [37] Influence of the Structure of Carbon Steels on the Corrosion, Hydrogenation, and Corrosion Cracking in Hydrogen-Sulfide Media
    M. S. Khoma
    V. R. Ivashkiv
    S. A. Halaichak
    M. R. Chuchman
    Kh. B. Vasyliv
    Materials Science, 2019, 55 : 272 - 276
  • [38] Influence of the Structure of Carbon Steels on the Corrosion, Hydrogenation, and Corrosion Cracking in Hydrogen-Sulfide Media
    Khoma, M. S.
    Ivashkiv, V. R.
    Halaichak, S. A.
    Chuchman, M. R.
    Vasyliv, Kh B.
    MATERIALS SCIENCE, 2019, 55 (02) : 266 - 270
  • [39] Passivity of corrosion-resistant alloys in environments containing chloride and hydrogen sulfide
    Denpo, K
    Ogawa, H
    CORROSION, 1997, 53 (09) : 718 - 723
  • [40] Multiple fracture of low-alloy steels in stages under hydrogen sulfide environment
    IMET im. A.A. Bajkova, Moscow, Russia
    Metalloved Term Obrab Met, 2 (14-22):
12345