Corrosion-mechanical fracture of tubing from carbon and alloy steels operating in environments containing hydrogen sulfide

被引：0
|
作者：
A. V. Ioffe
T. V. Tetyueva
M. A. Vyboishchik
S. A. Knyaz’kin
A. O. Zyryanov
机构：
[1] Samara Engineering-Technical Center,
[2] Tolyatti State University,undefined
来源：
Metal Science and Heat Treatment | 2013年 / 54卷
关键词：
sulfide stress corrosion cracking; tubing; field tests;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Comparative analysis of processes of corrosion-mechanical fracture of carbon and alloy steels in environments containing hydrogen sulfide is performed after laboratory (NACE TM0177) and field tests. The mechanism and kinetics of the evolution of fracture in steels of the two groups are considered.
引用
收藏
页码：492 / 497
页数：5
相关论文
共 50 条
  • [1] Corrosion-mechanical fracture of tubing from carbon and alloy steels operating in environments containing hydrogen sulfide
    Ioffe, A. V.
    Tetyueva, T. V.
    Vyboishchik, M. A.
    Knyaz'kin, S. A.
    Zyryanov, A. O.
    METAL SCIENCE AND HEAT TREATMENT, 2013, 54 (9-10) : 492 - 497
  • [2] Effect of inhibitors on the corrosion-mechanical fracture of steels in hydrogen-sulfide media
    Radkevych, OI
    Dominyuk, IM
    Tsynman, AI
    MATERIALS SCIENCE, 2002, 38 (01) : 126 - 131
  • [3] Effect of Inhibitors on the Corrosion-Mechanical Fracture of Steels in Hydrogen-Sulfide Media
    O. I. Radkevych
    I. M. Dominyuk
    A. I. Tsynman
    Materials Science, 2002, 38 : 126 - 131
  • [4] Corrosion-mechanical fracture of tube steels in operation
    A. V. Ioffe
    T. V. Tetyueva
    V. A. Revyakin
    E. A. Borisenkova
    S. A. Knyaz’kin
    T. V. Denisova
    Metal Science and Heat Treatment, 2013, 54 : 512 - 518
  • [5] Corrosion-mechanical fracture of tube steels in operation
    Ioffe, A. V.
    Tetyueva, T. V.
    Revyakin, V. A.
    Borisenkova, E. A.
    Knyaz'kin, S. A.
    Denisova, T. V.
    METAL SCIENCE AND HEAT TREATMENT, 2013, 54 (9-10) : 512 - 518
  • [6] Corrosion-mechanical resistance of pipe steel in hydrogen-sulfide containing media
    O. I. Radkevych
    O. S. P’yasets’kyi
    I. I. Vasylenko
    Materials Science, 2000, 36 : 425 - 430
  • [7] EFFECT OF HYDROGEN-SULFIDE AND LOW-TEMPERATURES ON THE TENDENCY OF CARBON-STEELS TO CORROSION-MECHANICAL DAMAGE
    KOVAL, VP
    ZAZULYAK, VA
    KOVALCHUK, RI
    PROTECTION OF METALS, 1979, 15 (01): : 67 - 69
  • [8] Identification of corrosion-mechanical fracture mechanism of structural steels
    Nykyforchyn, HM
    Tsyrulnyk, OT
    ECF 12: FRACTURE FROM DEFECTS, VOLS. I-III, 1998, : 1193 - 1198
  • [9] Corrosion-mechanical resistance of pipe steel in hydrogen-sulfide containing media
    Radkevych, OI
    P'yasets'kyi, OS
    Vasylenko, II
    MATERIALS SCIENCE, 2000, 36 (03) : 425 - 430
  • [10] EFFECT OF INHIBITORS ON THE CORROSION-MECHANICAL BEHAVIOR OF STEELS IN MEDIA CONTAINING HYDROGEN-SULFIDE AND SIMULATING THE EFFLUENTS OF THE PETROLEUM-INDUSTRY
    IVANOV, ES
    ZAVADSKAYA, VP
    GETMANSKII, MD
    KUZNETSOVA, GN
    JOURNAL OF APPLIED CHEMISTRY OF THE USSR, 1983, 56 (08): : 1624 - 1628
12345