Investigations of Solidification Structures of High Carbon Alloy Cast Steel Containing RE-V-Ti

被引:0
|
作者
Hanguang Fu
Yinhu Qu
Jiandong Xing
机构
[1] Xi’an Jiaotong University,State Key Laboratory for Mechanical Behavior of Materials, School of Materials Science and Engineering
[2] Xi’an Polytechnic University,School of Electromechanical Engineering
来源
Journal of Materials Engineering and Performance | 2009年 / 18卷
关键词
cast steel; rare earth; refinement; solidification structure; titanium;
D O I
暂无
中图分类号
学科分类号
摘要
The solidification microstructural characteristics of rare earth (RE) and vanadium and titanium-treated high carbon alloy cast steel, whose chemical compositions are 0.90 wt.% C, 3.0 wt.% Si, and 1.0 wt.% Mn, were investigated by means of optical microscopy (OM), scanning electron microscopy (SEM), electron probe microanalyzer (EPMA), and energy dispersive X-ray spectrometry (EDS). The alloys were prepared in an induction furnace. The results showed that compound additions of RE-V-Ti could obviously refine the solidification structures and decrease the diameter of grains. The average grain diameter of untreated high carbon alloy cast steel was 80 μm. The average grain diameter of high carbon alloy cast steel containing RE-V-Ti decreased to 40 μm. Finally, the reasons that RE-V-Ti refined the solidification structure were analyzed in detail.
引用
收藏
页码:333 / 338
页数:5
相关论文
共 50 条
  • [11] Structures and properties of high-carbon high speed steel by RE-Mg-Ti compound modification
    Fu, HG
    Fu, DM
    Zou, DN
    Xing, JD
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2004, 19 (02): : 48 - 51
  • [12] PRODUCTION OF HIGH QUALITY DIRECT CAST CARBON AND ALLOY STEEL BILLETS
    BROWN, DI
    JOURNAL OF METALS, 1965, 17 (04): : 426 - &
  • [13] Morphology of Solidification Structure and MnS Inclusion in High Carbon Steel Continuously Cast Bloom
    Luo, Sen
    Wang, Bingyu
    Wang, Zhaohui
    Jiang, Dongbin
    Wang, Weiling
    Zhu, Miaoyong
    ISIJ INTERNATIONAL, 2017, 57 (11) : 2000 - 2009
  • [14] Quantification of the Solidification Microstructure in Continuously-Cast High-Carbon Steel Billets
    Suvankar Ganguly
    S.K. Choudhary
    Metallurgical and Materials Transactions B, 2009, 40 : 397 - 404
  • [15] Quantification of the Solidification Microstructure in Continuously-Cast High-Carbon Steel Billets
    Ganguly, Suvankar
    Choudhary, S. K.
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2009, 40 (03): : 397 - 404
  • [16] KINETICS OF FERRITE TO AUSTENITE TRANSFORMATION IN A HIGH-STRENGTH LOW-ALLOY STEEL CONTAINING TI AND V
    JAYASWAL, SK
    GUPTA, SP
    ZEITSCHRIFT FUR METALLKUNDE, 1992, 83 (11): : 809 - 819
  • [17] Fractal Analysis of Solidification Microstructure of High Carbon High Alloy Cast Roll Manufactured by Centrifugal Casting
    Yamamoto, Masahiro
    Narita, Ichihito
    Miyahara, Hirofumi
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 2013, 99 (02): : 72 - 79
  • [18] NOZZLE CLOGGING IN HIGH-ALLOY STEEL CONTAINING TI AND AL
    SUDO, T
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 (04): : S162 - S162
  • [19] Effects of RE, V, Ti and B composite modification on the microstructure and properties of high chromium cast iron containing 3% molybdenum
    Guo Erjun
    Wang Lihua
    Wang Liping
    Huang Yongchang
    RARE METALS, 2009, 28 (06) : 606 - 611