Effect of hydrostatic pressure on the corrosion behaviour of Ni-Cr-Mo-V high strength steel

被引：119
|
作者：
Yang, Yange [1 ]
Zhang, Tao [1 ,2 ]
Shao, Yawei [1 ,2 ]
Meng, Guozhe [1 ,2 ]
Wang, Fuhui [1 ,2 ]
机构：
[1] Harbin Engn Univ, Corros & Protect Lab, Key Lab Superlight Mat & Surface Technol, Minist Educ, Harbin 150001, Peoples R China
[2] Chinese Acad Sci, State Key Lab Corros & Protect, Inst Met Res, Shenyang 110016, Peoples R China
来源：
CORROSION SCIENCE | 2010年 / 52卷 / 08期
基金：
中国国家自然科学基金;
关键词：
Low alloy steel; EIS; SEM; Weight loss; SLIGHTLY ALKALINE-SOLUTIONS; WATER CATHODIC PROTECTION; RECURRENCE PLOTS; SEA-WATER; PITTING CORROSION; STAINLESS-STEELS; ALUMINUM; RESISTANCE; INITIATION; MAGNESIUM;
D O I：
10.1016/j.corsci.2010.04.025
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Effect of hydrostatic pressure on the corrosion behaviour of Ni-Cr-Mo-V high strength steel was investigated by electrochemical measurements and SEM observation. The electrochemical noise (EN) data was analyzed based on non-linear dynamic theory. The experimental results revealed that hydrostatic pressure decreased the corrosion resistance of Ni-Cr-Mo-V steel and the corrosion at high hydrostatic pressure was more uniform due to the higher initiation rate and lower growth probability of metastable pitting. (C) 2010 Elsevier Ltd. All rights reserved.
引用
收藏
页码：2697 / 2706
页数：10
相关论文
共 50 条
  • [21] THE ROLE OF MN IN THE TEMPER EMBRITTLEMENT OF A 3.5 NI-CR-MO-V STEEL
    SMITH, JF
    REYNOLDS, JH
    SOUTHWORTH, HN
    ACTA METALLURGICA, 1980, 28 (11): : 1555 - 1564
  • [22] Effect of Solidification Segregation on Microstructure and Mechanical Properties of a Ni-Cr-Mo-V Steel Weld Metal
    Han, Chaoyu
    Liu, Qu
    Cai, Zhipeng
    Huo, Xin
    Fan, Manjie
    Li, Kejian
    Pan, Jiluan
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2022, 53 (04): : 1394 - 1406
  • [23] Hot Deformation Behavior and Dynamic Recrystallization Characteristics in a Low-Alloy High-Strength Ni-Cr-Mo-V Steel
    Wu, Chuan
    Han, Shuang
    ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2018, 31 (09) : 963 - 974
  • [24] The effect of microstructure on the fatigue crack growth behavior of Ni-Cr-Mo-V steel weld metal
    Han, Chaoyu
    Liu, Qu
    Cai, Zhipeng
    Sun, Qixing
    Huo, Xin
    Fan, Manjie
    Li, Kejian
    Pan, Jiluan
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 176
  • [25] EFFECT OF AN INTERCRITICAL HEAT-TREATMENT ON TEMPER EMBRITTLEMENT OF A NI-CR-MO-V ROTOR STEEL
    WADA, T
    DOANE, DV
    METALLURGICAL TRANSACTIONS, 1974, 5 (01): : 231 - 239
  • [26] Effect of Solidification Segregation on Microstructure and Mechanical Properties of a Ni-Cr-Mo-V Steel Weld Metal
    Chaoyu Han
    Qu Liu
    Zhipeng Cai
    Xin Huo
    Manjie Fan
    Kejian Li
    Jiluan Pan
    Metallurgical and Materials Transactions A, 2022, 53 : 1394 - 1406
  • [27] Microstructural evolution and mechanical properties of a low alloy high strength Ni-Cr-Mo-V steel during heat treatment process
    Wu, C.
    Han, S.
    INTERNATIONAL CONFERENCE ON COMPUTER INFORMATION AND AUTOMATION ENGINEERING, 2018, 359
  • [28] INFLUENCE OF PRE-EXISTING PITS ON FATIGUE-CORROSION OF A LOW NI-CR-MO-V STEEL ALLOY
    LEYMONIE, C
    MOLIERE, M
    RIOLLET, G
    THAUVIN, G
    VERDIER, Y
    VITTEMANT, B
    COMPTES RENDUS DE L ACADEMIE DES SCIENCES SERIE II, 1989, 308 (13): : 1149 - 1152
  • [29] THE BEHAVIOR OF MULTIPLE STRESS-CORROSION CRACKS IN A MN-CR AND A NI-CR-MO-V STEEL .1. METALLOGRAPHY
    WANG, YZ
    EBTEHAJ, K
    HARDIE, D
    PARKINS, RN
    CORROSION SCIENCE, 1995, 37 (11) : 1651 - 1675
  • [30] Development of a Ni-Cr-Mo-V Alloyed Ductile Iron with High Hardness
    Yang, Chao
    Gao, Zhijie
    Du, Yuzhou
    Wang, Ke
    Jiang, Bailing
    INTERNATIONAL JOURNAL OF METALCASTING, 2024, 18 (02) : 1677 - 1685
12345