Comparison of magnetic properties of austenitic stainless steel after ion irradiation

被引：3
|
作者：
Xu, Chaoliang [1 ]
Liu, Xiangbing [1 ]
Xue, Fei [1 ]
Li, Yuanfei [1 ]
Qian, Wangjie [1 ]
机构：
[1] Suzhou Nucl Power Res Inst, Suzhou 215004, Jiangsu, Peoples R China
来源：
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS | 2018年 / 427卷
基金：
中国国家自然科学基金;
关键词：
Austenitic stainless steel; Irradiation; Magnetization; Martensite; Coercivity; MARTENSITIC-TRANSFORMATION; TEMPERATURE; XE; IMPLANTATION; CRACKING; REACTOR; ALLOYS; SENSOR; IASCC; IRON;
D O I：
10.1016/j.nimb.2018.04.041
中图分类号：
TH7 [仪器、仪表];
学科分类号：
0804 ; 080401 ; 081102 ;
摘要：
Specimens of austenitic stainless steel (ASS) were irradiated with H, Fe and Xe ions at room temperature. The vibrating sample magnetometer (VSM) and grazing incidence X-ray diffraction (GIXRD) were used to analyze the magnetic properties and martensite formation. The magnetic hysteresis loops indicated that higher irradiation damage causes more significant magnetization phenomenon. Under the same damage level, Xe irradiation causes the most significant magnetization, Fe irradiation is the second, and H irradiation is the least. A similar martensite amount variation with irradiation can be obtained. The coercivity H-c increases first to 2 dpa and then decreases continuously with irradiation damage for Xe irradiation. At the same damage lever, H irradiation causes a largest H-c and Xe irradiation causes a minimal one.
引用
收藏
页码：87 / 90
页数：4
相关论文
共 50 条
  • [41] Structure and Deformation Properties of Austenitic Stainless Steel
    N. S. Surikova
    I. V. Vlasov
    N. A. Narkevich
    A. I. Gordienko
    P. V. Kuznetsov
    Physics of Metals and Metallography, 2020, 121 : 276 - 283
  • [42] Fatigue properties of notched austenitic stainless steel
    Hattori, N
    Nishida, S
    Yano, Y
    Yamamoto, A
    EXPERIMENTAL MECHANICS, VOLS 1 AND 2: ADVANCES IN DESIGN, TESTING AND ANALYSIS, 1998, : 1103 - 1108
  • [43] Structure and Deformation Properties of Austenitic Stainless Steel
    Surikova, N. S.
    Vlasov, I. V.
    Narkevich, N. A.
    Gordienko, A., I
    Kuznetsov, P., V
    PHYSICS OF METALS AND METALLOGRAPHY, 2020, 121 (03): : 276 - 283
  • [44] Austenitic Steel Magnetic Properties Evaluation After Mechanical Deformation
    Smetana, Milan
    Capova, Klara
    Palcek, Peter
    ELECTROMAGNETIC NONDESTRUCTIVE EVALUATION (XVIII), 2015, 40 : 35 - 42
  • [45] THE DOSE DEPENDENCE OF INERT GASES IRRADIATION HARDENING OF 316 AUSTENITIC STAINLESS STEEL AFTER LOW TEMPERATURE IRRADIATION
    Karpov, S. A.
    Tolstolutskaya, G. D.
    Voyevodin, V. N.
    Tolmachova, G. N.
    Kopanets, I. E.
    PROBLEMS OF ATOMIC SCIENCE AND TECHNOLOGY, 2018, (05): : 34 - 39
  • [46] Improvement in corrosion resistance of austenitic stainless steel by laser irradiation
    Zamfir, Simona
    Vidu, Ruxandra
    IPB Buletin Stiintific - Chemistry and Materials Science, 1992, 54 (1-2):
  • [47] Further investigation of the structure and properties of austenitic stainless steel after plasma nitriding
    Menthe, E
    Rie, KT
    SURFACE & COATINGS TECHNOLOGY, 1999, 116 : 199 - 204
  • [48] Creep properties of metastable austenitic stainless steel wires after cold drawing
    Schmidt, Werner
    Domalski, Hans-Heinrich
    Wire, 1988, 38 (06): : 593 - 598
  • [49] DEVELOPMENT OF MICROSTRUCTURE AND MECHANICAL PROPERTIES OF AUSTENITIC STAINLESS STEEL AFTER ECAP DEFORMATION
    Greger, Miroslav
    Kander, Ladislav
    METAL 2013: 22ND INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2013, : 431 - 437
  • [50] Investigation of properties of ion-nitrided AISI 304 austenitic-stainless steel
    Sahin, Mumin
    Sevil, Ceyhun
    INDUSTRIAL LUBRICATION AND TRIBOLOGY, 2011, 63 (05) : 359 - 366
12345